Amine-Modified Mesoporous Magnesium Carbonate as an Effective Adsorbent for Azo Dyes

↓ Direkt till sidans innehåll
↓ Direkt till sidans sekundära innehåll (sidomenyn)

Sökning: WFRF:(Strømme Maria) > Amine-Modified Meso...

Vall, MariaUppsala universitet,Nanoteknologi och funktionella material (författare)

Amine-Modified Mesoporous Magnesium Carbonate as an Effective Adsorbent for Azo Dyes

Artikel/kapitelEngelska2019

Förlag, utgivningsår, omfång ...

2019-02-11
American Chemical Society (ACS),2019
electronicrdacarrier

Nummerbeteckningar

LIBRIS-ID:oai:DiVA.org:uu-380594
https://urn.kb.se/resolve?urn=urn:nbn:se:uu:diva-380594URI
https://doi.org/10.1021/acsomega.8b03493DOI

Kompletterande språkuppgifter

Språk:engelska
Sammanfattning på:engelska

Ingår i deldatabas

SwePubSwePub

Klassifikation

Ämneskategori:ref swepub-contenttype
Ämneskategori:art swepub-publicationtype

Anmärkningar

Mesoporous magnesium carbonate (MMC) was evaluated as a potential candidate material for removal of dyes from textile industry wastewater. The adsorption property of MMC was analyzed for three different azo dyes: reactive black 5 (RB5), amaranth (AM), and acid red 183 (AR183). Further, the effect of porosity, amine modification, ionic strength, and pH was evaluated. MMC modified with 3-(aminopropyl)triethoxysilane (aMMC) showed consistently high uptake levels for all of the azo dyes tested; the uptake of RB5, AM, and AR183 was ∼360, ∼143 and ∼170 mg/g, respectively. The results demonstrated the importance of porosity and surface chemistry in the effective adsorption of the azo dye in aqueous systems. The uptake of RB5 and AM on aMMC was not significantly affected by pH (when varied between 4 and 10), although reduced uptake of RB5 and AM was observed at pH values <2 and >12. The addition of NaCl salt at concentrations up to 1000 mM had minimal effect on the high uptake of RB5 on aMMC. The uptake of AM by aMMC was reduced by approximately 20% in the presence of NaCl even at low concentrations. The uptake of AR183 by aMMC varied noticeably by changes in pH and no specific trend was observed. The presence of NaCl also adversely affected the uptake of AR183 on aMMC. The adsorption of the azo dye on aMMC was most likely driven by electrostatic interactions. We show here that aMMC is a potential candidate adsorbent for the effective removal of azo dyes from textile wastewaters.

Ämnesord och genrebeteckningar

TEKNIK OCH TEKNOLOGIER Nanoteknik hsv//swe
ENGINEERING AND TECHNOLOGY Nano-technology hsv//eng
Teknisk fysik med inriktning mot nanoteknologi och funktionella material
Engineering Science with specialization in Nanotechnology and Functional Materials

Biuppslag (personer, institutioner, konferenser, titlar ...)

Strömme, Maria,1970-Uppsala universitet,Nanoteknologi och funktionella material(Swepub:uu)mst26208 (författare)
Cheung, OceanUppsala universitet,Nanoteknologi och funktionella material(Swepub:uu)ocech274 (författare)
Uppsala universitetNanoteknologi och funktionella material (creator_code:org_t)

Sammanhörande titlar

Ingår i:ACS Omega: American Chemical Society (ACS)4:2, s. 2973-29792470-1343

Internetlänk

Hitta via bibliotek

ACS Omega (Sök värdpublikationen i LIBRIS)

Till lärosätets databas

Hitta mer i SwePub

Av författaren/redakt...: Vall, Maria; Strömme, Maria, ...; Cheung, Ocean

Om ämnet

TEKNIK OCH TEKNOLOGIER: TEKNIK OCH TEKNO ...; och Nanoteknik

Artiklar i publikationen: ACS Omega

Av lärosätet: Uppsala universitet

Sök utanför SwePub

Sök vidare i:: Google; Google Book Search; Google Scholar

Kungliga biblioteket hanterar dina personuppgifter i enlighet med EU:s dataskyddsförordning (2018), GDPR. Läs mer om hur det funkar här.
Så här hanterar KB dina uppgifter vid användning av denna tjänst.

LIBRIS.kb.se