Multi-component (Al,Cr,Nb,Y,Zr)N thin films by reactive magnetron sputter deposition for increased hardness and corrosion resistance

• Multi-component nitride thin films in the Al-Cr-Nb-Y-Zr system with non-equimolar composition have been deposited by reactive dc magnetron sputtering. The substrate temperature and substrate bias have been varied, from room temperature to 700 degrees C and from 0 to -200 V respectively. The relationship between these varied growth conditions on the structure, morphology, mechanical and corrosion properties of the films have been probed. All films consisted of a single solid solution with a NaCl-type structure, as shown by X-ray diffraction. However, elemental energy dispersive spectroscopy maps, obtained in the scanning transmission electron microscope, indicated that there could be partial segregation of Al, Cr and Y atoms within the grains. The microstructure of the films became denser, more fine-grained and smoother as the bias and temperature were increased. Nanoindentation showed that the hardness of the films increased with both bias and temperature, reaching a maximum of 27 +/- 2 GPa. The corrosion resistance of the films, studied by performing potentiodynamic polarisation curves in 1 M HCl, was also found to be improved when compared to a commercially available hyper-duplex stainless steel and a ternary reference (Nb,Zr)N thin film as well.

Ämnesord

NATURVETENSKAP  -- Kemi -- Oorganisk kemi (hsv//swe)

NATURAL SCIENCES  -- Chemical Sciences -- Inorganic Chemistry (hsv//eng)

Publikations- och innehållstyp

ref (ämneskategori)

art (ämneskategori)