Phase composition and transformations in magnetron-sputtered (Al,V)2O3 coatings
-
- Landälv, Ludvig, 1982- (författare)
- Linköpings universitet,Tunnfilmsfysik,Tekniska fakulteten,Sandvik Coromant AB, Stockholm, Sweden
-
- Carlström, C-F (författare)
- Sandvik Coromant AB, Stockholm, Sweden
-
- Li, J. (författare)
- Linköping Univ, Thin Film Phys Div, Dept Phys Chem & Biol IFM, Linköping, Sweden
-
visa fler...
-
- Primetzhofer, Daniel (författare)
- Uppsala universitet,Tillämpad kärnfysik,Applied Nuclear Physics, Department of Physics and Astronomy, Uppsala University, Uppsala, Sweden
-
- Jõesaar, M. J. (författare)
- SECO Tools AB, Fagersta, Sweden
-
- Ahlgren, M. (författare)
- Sandvik Coromant AB, Stockholm, Sweden
-
- Göthelid, E. (författare)
- Sandvik Coromant AB, Stockholm, Sweden
-
- Alling, Björn, 1980- (författare)
- Linköpings universitet,Teoretisk Fysik,Tekniska fakulteten
-
- Hultman, Lars, Professor, 1960- (författare)
- Linköpings universitet,Tunnfilmsfysik,Tekniska fakulteten
-
- Eklund, Per, Docent, 1977- (författare)
- Linköpings universitet,Tunnfilmsfysik,Tekniska fakulteten
-
- Lu, Jun, 1962- (författare)
- Linköpings universitet,Tunnfilmsfysik,Tekniska fakulteten
-
visa färre...
-
(creator_code:org_t)
- Elsevier BV, 2019
- 2019
- Engelska.
-
Ingår i: Thin Solid Films. - : Elsevier BV. - 0040-6090 .- 1879-2731. ; 688
- Relaterad länk:
-
http://arxiv.org/pdf...
-
visa fler...
-
https://arxiv.org/ab...
-
https://liu.diva-por... (primary) (Raw object)
-
https://urn.kb.se/re...
-
https://doi.org/10.1...
-
https://urn.kb.se/re...
-
visa färre...
Abstract
Ämnesord
Stäng
- Coatings of (Al1-xVx)2O3, with x ranging from 0 to 1, were deposited by pulsed DC reactive sputter deposition on Si(100) at a temperature of 550 °C. XRD showed three different crystal structures depending on V-metal fraction in the coating: α-V2O3 rhombohedral structure for 100 at.% V, a defect spinel structure for the intermediate region, 63–42 at.% V. At lower V-content, 18 and 7 at.%, a gamma-alumina-like solid solution was observed, shifted to larger d-spacing compared to pure γ-Al2O3. The microstructure changes from large columnar faceted grains for α-V2O3 to smaller equiaxed grains when lowering the vanadium content towards pure γ-Al2O3. Annealing in air resulted in formation of V2O5 crystals on the surface of the coating after annealing to 500 °C for 42 at.% V and 700 °C for 18 at.% V metal fraction respectively. The highest thermal stability was shown for pure γ-Al2O3-coating, which transformed to α-Al2O3 after annealing to 1100 °C. Highest hardness was observed for the Al-rich oxides, ~24 GPa. The latter decreased with increasing V-content, larger than 7 at.% V metal fraction. The measured hardness after annealing in air decreased in conjunction with the onset of further oxidation of the coatings.
Ämnesord
- TEKNIK OCH TEKNOLOGIER -- Materialteknik -- Bearbetnings-, yt- och fogningsteknik (hsv//swe)
- ENGINEERING AND TECHNOLOGY -- Materials Engineering -- Manufacturing, Surface and Joining Technology (hsv//eng)
- NATURVETENSKAP -- Fysik (hsv//swe)
- NATURAL SCIENCES -- Physical Sciences (hsv//eng)
Nyckelord
- Aluminum vanadium oxide
- Pulsed DC magnetron sputtering
- Annealing
- V2O5
- AlVO4
- AlVO3
Publikations- och innehållstyp
- ref (ämneskategori)
- art (ämneskategori)
Hitta via bibliotek
Till lärosätets databas
- Av författaren/redakt...
-
Landälv, Ludvig, ...
-
Carlström, C-F
-
Li, J.
-
Primetzhofer, Da ...
-
Jõesaar, M. J.
-
Ahlgren, M.
-
visa fler...
-
Göthelid, E.
-
Alling, Björn, 1 ...
-
Hultman, Lars, P ...
-
Eklund, Per, Doc ...
-
Lu, Jun, 1962-
-
visa färre...
- Om ämnet
-
- TEKNIK OCH TEKNOLOGIER
-
TEKNIK OCH TEKNO ...
-
och Materialteknik
-
och Bearbetnings yt ...
-
- NATURVETENSKAP
-
NATURVETENSKAP
-
och Fysik
- Artiklar i publikationen
-
Thin Solid Films
- Av lärosätet
-
Uppsala universitet
-
Linköpings universitet