  • Azina, ClioLinköpings universitet,Tunnfilmsfysik,Tekniska fakulteten,Rhein Westfal TH Aachen, Germany (författare)

Oxidation behaviour of V2AlC MAX phase coatings

  • Artikel/kapitelEngelska2020

Förlag, utgivningsår, omfång ...

  • ELSEVIER SCI LTD,2020
  • electronicrdacarrier

Nummerbeteckningar

  • LIBRIS-ID:oai:DiVA.org:uu-418720
  • https://urn.kb.se/resolve?urn=urn:nbn:se:uu:diva-418720URI
  • https://doi.org/10.1016/j.jeurceramsoc.2020.05.080DOI
  • https://urn.kb.se/resolve?urn=urn:nbn:se:liu:diva-167628URI

Kompletterande språkuppgifter

  • Språk:engelska
  • Sammanfattning på:engelska

Ingår i deldatabas

Klassifikation

  • Ämneskategori:ref swepub-contenttype
  • Ämneskategori:art swepub-publicationtype

Anmärkningar

  • Funding Agencies|Euratom research and training programme 2014-2018 [740415]; Swedish Government Strategic Research Area in Materials Science on Functional Materials at Linkoping University (Faculty Grant SFO-Mat-LiU) [2009 00971]; Foundation Olle Engkvist Byggmastare [184-561]; Swedish research council, VR-RFISwedish Research Council [821-2012-5144, 2017-00646_9]; Swedish Foundation for Strategic Research (SSF)Swedish Foundation for Strategic Research [RIF14-0053]; Swedish Research Council VR Grant [2018-03957]; Swedish Research Council VINNOVA grant [2019-04882]; International Union for Vacuum Science, Technique and Applications through the Medard W. Welch International Scholarship 2019
  • We report on the oxidation behaviour of V2AlC coatings up to 800 degrees C, in air. The coatings were deposited at 580 degrees C using magnetron sputtering from a powder metallurgical composite V2AlC target and were subsequently oxidised for 5, 15 and 30 min. The microstructural evolution of the samples was investigated, and X-ray diffraction patterns were collected to track the formation of oxides. The first indications of oxidation appear after just 15 min at 500 degrees C, as V-based oxides grew on the surface of the coatings. Later, the presence of mostly V-based oxides and ternary (V, Al)-oxides was observed starting after 5 min at 600 degrees C. Further analyses confirmed outward diffusion of V and inward diffusion of O, while Al tends to sublimate. alpha-A12O3 was only indexed after 5 min at 800 degrees C. Ex-situ electrical resistivity measurements allowed tracking the oxidation progress of the V2AlC coating.

Ämnesord och genrebeteckningar

Biuppslag (personer, institutioner, konferenser, titlar ...)

  • Mraz, StanislavRhein Westfal TH Aachen, Mat Chem, Kope 10, D-52074 Aachen, Germany. (författare)
  • Greczynski, GrzegorzLinköpings universitet,Tunnfilmsfysik,Tekniska fakulteten(Swepub:liu)grzgr49 (författare)
  • Hans, MarcusRhein Westfal TH Aachen, Mat Chem, Kope 10, D-52074 Aachen, Germany. (författare)
  • Primetzhofer, DanielUppsala universitet,Tillämpad kärnfysik,Uppsala Univ, Sweden(Swepub:uu)danpr521 (författare)
  • Schneider, Jochen M.Rhein Westfal TH Aachen, Mat Chem, Kope 10, D-52074 Aachen, Germany. (författare)
  • Eklund, PerLinköpings universitet,Tunnfilmsfysik,Tekniska fakulteten(Swepub:liu)perek02 (författare)
  • Linköpings universitetTunnfilmsfysik (creator_code:org_t)

Sammanhörande titlar

  • Ingår i:Journal of the European Ceramic Society: ELSEVIER SCI LTD40:13, s. 4436-44440955-22191873-619X

Internetlänk

Hitta via bibliotek

Till lärosätets databas

Kungliga biblioteket hanterar dina personuppgifter i enlighet med EU:s dataskyddsförordning (2018), GDPR. Läs mer om hur det funkar här.
Så här hanterar KB dina uppgifter vid användning av denna tjänst.

 
pil uppåt Stäng

Kopiera och spara länken för att återkomma till aktuell vy