Influence of Ta on the oxidation resistance of WB2-z coatings

• Ternary W1-x TaxB2-z is a promising protective coating material possessing enhanced ductile character and phase stability compared to closely related binaries. Here, the oxidation resistance of W1-xTaxB2-z thin films was experimentally investigated at temperatures up to 700 degrees C. Ta alloying in sputter deposited WB2-z coatings led to decelerated oxide scale growth and a changed growth mode from paralinear to a more linear (but retarded) behavior with increasing Ta content. The corresponding rate constants decrease from k(p)* = 6.3.10(-4) mu m(2)/s for WB2-z to k(p)* = 1.1.10(-4) mu m(2)/s for W0.66Ta0.34B2-z as well as k(1) = 2.6.10(-5) mu m/s for TaB2-z, underlined by decreasing scale thicknesses ranging from 1170 nm (WB2-z), over 610 nm (W0.66Ta0.34B2-z) to 320 nm (TaB2-z) after 10 min at 700 degrees C. Dense and adherent scales exhibit an increased tantalum content (columnar oxides), which suppresses the volatile character of tungsten-rich as well as boron oxides, hence being a key-factor for enhanced oxidation resistance. Thus, adding Ta (in the range of x = 0.2-0.3) to a-structured WB2-z does not only positively influence the ductile character and thermal stability but also drastically increases the oxidation resistance.

Ämnesord

NATURVETENSKAP  -- Kemi -- Materialkemi (hsv//swe)

NATURAL SCIENCES  -- Chemical Sciences -- Materials Chemistry (hsv//eng)

Nyckelord

Oxidation resistance

Transition metal diborides

Scale growth

Diborides

Publikations- och innehållstyp

ref (ämneskategori)

art (ämneskategori)