Influence of the nitrogen content on the corrosion resistances of multicomponent AlCrNbYZrN coatings

• In this study, the relationship between the nitrogen content and the corrosion resistances of non-equimolar multicomponent AlCrNbYZrN films (N = 13-49 at.%) is probed. While there was no linear relationship between nitrogen content and corrosion resistance, the results clearly show that the corrosion resistances of the films were instead determined by their nitrogen-induced porosities i.e. the less porous the sample, the higher the corrosion resistance. The 23, 30 and 37 at.% N samples were denser while the 13 at.% N sample was porous and the 49 at.% N film had an underdense nanocrystalline columnar cross section permitting the ingress of electrolyte.

Subject headings

TEKNIK OCH TEKNOLOGIER  -- Kemiteknik -- Korrosionsteknik (hsv//swe)

ENGINEERING AND TECHNOLOGY  -- Chemical Engineering -- Corrosion Engineering (hsv//eng)

NATURVETENSKAP  -- Kemi -- Oorganisk kemi (hsv//swe)

NATURAL SCIENCES  -- Chemical Sciences -- Inorganic Chemistry (hsv//eng)

NATURVETENSKAP  -- Kemi -- Materialkemi (hsv//swe)

NATURAL SCIENCES  -- Chemical Sciences -- Materials Chemistry (hsv//eng)

Keyword

Multicomponent alloy

Multi-principal element nitride

Corrosion

Porosity

X-ray photoelectron spectroscopy

Publication and Content Type

ref (subject category)

art (subject category)