Monitoring of epitaxial graphene anodization

• Anodization of a graphene monolayer on silicon carbide was monitored with electrochemical impedance spectroscopy. Structural and functional changes of the material were observed by Raman spectroscopy and voltammetry. A 21 fold increase of the specific capacitance of graphene was observed during the anodization. An electrochemical kinetic study of the Fe(CN)(6)(3) (/4) redox couple showed a slow irreversible redox process at the pristine graphene, but after anodization the reaction rate increased by several orders of magnitude. On the other hand, the Ru(NH3) (3+/2+)(6) redox couple proved to be insensitive to the activation process. The results of the electron transfer kinetics correlate well with capacitance measurements. The Raman mapping results suggest that the increased specific capacitance of the anodized sample is likely due to a substantial increase of electron doping, induced by defect formation, in the monolayer upon anodization. The doping concentration increased from less than 1 x 10(13) of the pristine graphene to 4-8 x 10(13) of the anodized graphene. (C) 2017 Elsevier Ltd. All rights reserved.

Ämnesord

NATURVETENSKAP  -- Fysik -- Den kondenserade materiens fysik (hsv//swe)

NATURAL SCIENCES  -- Physical Sciences -- Condensed Matter Physics (hsv//eng)

Nyckelord

Epitaxial graphene; Graphene monolayer; Anodization; Electrode kinetics; Raman spectroscopy; voltammetry; Electrochemical impedance spectroscopy

Publikations- och innehållstyp

ref (ämneskategori)

art (ämneskategori)