Li insertion in sol-gel prepared Mn-doped TiO2 studied by electron spectroscopy in ultrahigh vacuum

The properties of a sol-gel prepared Mn-modified TiO2 film have been studied with X-ray absorption spectroscopy (XAS) and photoelectron spectroscopy (PES) using synchrotron radiation. The chemical composition and oxidation state of the elements have been determined. The manganese content estimated by PES of the Mn-modified film is about 10% and both Mn2+ and Mn3+ are observed. Addition of Mn is found to modify the valence band edge. The Mn 3d states are found to extend about 1 eV into the TiO 2 band gap region. It is demonstrated that lithium insertion into the sol-gel film can be performed in a stepwise fashion in situ under ultrahigh vacuum (UHV) conditions. Lithium is distributed evenly throughout the entire film and leads to reduction of Mn3+ to Mn2+ followed by reduction of Ti4+ to Ti3+. The XAS and PES measurements give fully consistent results regarding the amount of inserted lithium.

Karlsson, Patrik G.Uppsala universitet,Fysik I (författare)
Westin, GunnarUppsala universitet,Institutionen för materialkemi(Swepub:uu)guwes093 (författare)
Blomquist, JakobLund University,Lunds universitet,Kemisk fysik,Enheten för fysikalisk och teoretisk kemi,Kemiska institutionen,Institutioner vid LTH,Lunds Tekniska Högskola,Chemical Physics,Physical and theoretical chemistry,Department of Chemistry,Departments at LTH,Faculty of Engineering, LTH(Swepub:lu)chem-jbl (författare)
Uvdal, PerLund University,Lunds universitet,Kemisk fysik,Enheten för fysikalisk och teoretisk kemi,Kemiska institutionen,Institutioner vid LTH,Lunds Tekniska Högskola,Chemical Physics,Physical and theoretical chemistry,Department of Chemistry,Departments at LTH,Faculty of Engineering, LTH(Swepub:lu)chph-puv (författare)
Siegbahn, HansUppsala universitet,Fysik I(Swepub:uu)hsi13487 (författare)
Sandell, AndersUppsala universitet,Fysik I (författare)
Uppsala universitetFysik I (creator_code:org_t)

Ingår i:The Journal of Physical Chemistry C: American Chemical Society (ACS)111:8, s. 3459-34661932-74471932-7455

Av författaren/redakt...: Richter, Jan Hin ...; Karlsson, Patrik ...; Westin, Gunnar; Blomquist, Jakob; Uvdal, Per; Siegbahn, Hans; visa fler...; Sandell, Anders; visa färre...

Om ämnet

Kungliga biblioteket hanterar dina personuppgifter i enlighet med EU:s dataskyddsförordning (2018), GDPR. Läs mer om hur det funkar här.
Så här hanterar KB dina uppgifter vid användning av denna tjänst.