Fabrication of individual, vertically aligned carbon nanofibres on metal substrates from prefabricated catalyst dots
-
- Kabir, Mohammad, 1974 (författare)
- Chalmers tekniska högskola,Chalmers University of Technology
-
- Morjan, Raluca. E., 1976 (författare)
- Göteborgs universitet,University of Gothenburg
-
- Nerushev, Oleg, 1960 (författare)
- Gothenburg University,Göteborgs universitet,Institutionen för fysik (GU),Department of Physics (GU),University of Gothenburg
-
visa fler...
-
- Lundgren, Per, 1968 (författare)
- Chalmers tekniska högskola,Chalmers University of Technology
-
- Bengtsson, Stefan, 1961 (författare)
- Chalmers tekniska högskola,Chalmers University of Technology
-
- Enoksson, Peter, 1957 (författare)
- Chalmers tekniska högskola,Chalmers University of Technology
-
- Campbell, Eleanor E B, 1960 (författare)
- Gothenburg University,Göteborgs universitet,Institutionen för fysik (GU),Department of Physics (GU),University of Gothenburg
-
visa färre...
-
(creator_code:org_t)
- 2006-01-10
- 2006
- Engelska.
-
Ingår i: Nanotechnology. - : IOP Publishing. - 0957-4484 .- 1361-6528. ; 17:3, s. 790-794
- Relaterad länk:
-
http://dx.doi.org/10...
-
visa fler...
-
https://gup.ub.gu.se...
-
https://doi.org/10.1...
-
https://research.cha...
-
visa färre...
Abstract
Ämnesord
Stäng
- Carbon nanofibres (CNFs) of controlled diameter and length were grown on different metal substrates using plasma-enhanced chemical vapour deposition (PECVD). The diameter control of catalyst dots (and hence CNF diameter) was obtained by using the shot modulation technique in electron beam lithography. Catalyst dots of different sizes within arrays of different pitch were prepared and the dependence of the growth of vertically aligned CNFs on these parameters was studied for different metal underlayers. Good quality vertically aligned CNFs with a narrow length distribution were grown on Mo and W substrates. The structures grown on Nb substrates were significantly shorter for identical growth conditions and showed a lower nucleation rate. We demonstrate that through the shot modulation technique it is possible to control the diameter variation of CNFs from a single design geometry for the catalyst deposition. Individual VACNFs can be grown down to a pitch within the range 100–500 nm.
Ämnesord
- TEKNIK OCH TEKNOLOGIER -- Annan teknik -- Övrig annan teknik (hsv//swe)
- ENGINEERING AND TECHNOLOGY -- Other Engineering and Technologies -- Other Engineering and Technologies not elsewhere specified (hsv//eng)
- NATURVETENSKAP -- Fysik -- Den kondenserade materiens fysik (hsv//swe)
- NATURAL SCIENCES -- Physical Sciences -- Condensed Matter Physics (hsv//eng)
Nyckelord
- carbon nanotubes nanofibres
- carbon nanotubes nanofibres
Publikations- och innehållstyp
- ref (ämneskategori)
- art (ämneskategori)
Hitta via bibliotek
Till lärosätets databas
- Av författaren/redakt...
-
Kabir, Mohammad, ...
-
Morjan, Raluca. ...
-
Nerushev, Oleg, ...
-
Lundgren, Per, 1 ...
-
Bengtsson, Stefa ...
-
Enoksson, Peter, ...
-
visa fler...
-
Campbell, Eleano ...
-
visa färre...
- Om ämnet
-
- TEKNIK OCH TEKNOLOGIER
-
TEKNIK OCH TEKNO ...
-
och Annan teknik
-
och Övrig annan tekn ...
-
- NATURVETENSKAP
-
NATURVETENSKAP
-
och Fysik
-
och Den kondenserade ...
- Artiklar i publikationen
-
Nanotechnology
- Av lärosätet
-
Göteborgs universitet
-
Chalmers tekniska högskola