A study of the influence of grain boundaries on short crack growth during varying load using a dislocation technique

• The propagation of short cracks in the neighbourhood of grain boundaries have been investigated using a technique were the crack is modelled by distributed dislocation dipoles and the plastic deformation is represented by discrete dislocations. Discrete dislocations are emitted from the crack tip as the crack grows. Dislocations can also nucleate at the grain boundaries. The influence on crack growth characteristics of the distance between the initial crack tip and the grain boundary has been studied. It was found that crack growth rate is strongly correlated to the dislocation pile-ups at the grain boundaries. (C) 2004 Elsevier Ltd. All rights reserved.

Ämnesord

TEKNIK OCH TEKNOLOGIER  -- Materialteknik (hsv//swe)

ENGINEERING AND TECHNOLOGY  -- Materials Engineering (hsv//eng)

TEKNIK OCH TEKNOLOGIER  -- Maskinteknik -- Teknisk mekanik (hsv//swe)

ENGINEERING AND TECHNOLOGY  -- Mechanical Engineering -- Applied Mechanics (hsv//eng)

Nyckelord

boundary

grain

short crack growth

dislocation dipoles

discrete dislocations

dislocation nucleation

dislocation dipoles

Publikations- och innehållstyp

art (ämneskategori)

ref (ämneskategori)