Structure and Characterization of KSc(BH4)(4)

• A new potassium scandium borohydride, KSc(BH4)(4), is presented and characterized by a combination of in situ synchrotron radiation powder X-ray diffraction, thermal analysis, and vibrational and NMR spectroscopy. The title compound, KSc(BH4)(4), forms at ambient conditions in ball milled mixtures of potassium borohydride and ScCl3 together with a new ternary chloride K3ScCl6, which is also structurally characterized. This indicates that the formation of KSc(BH4)(4) differs from a simple metathesis reaction, and the highest scandium borohydride yield (similar to 31 mol %) can be obtained with a reactant ratio KBH4:ScCl3 of 2:1. KSc(BH4)(4) crystallizes in the orthorhombic crystal system, a = 11.856(5), b = 7.800(3), c = 10.126(6) angstrom, v = 936.4(8) angstrom(3) at RT, with the space group symmetry Prima. KSc(BH4)(4) has a BaSO4 type structure where the BH4 tetrahedra take the oxygen positions. Regarding the packing of cations, K+, and complex anions, [Sc(BH4)(4)](-), the structure of KSc(BH4)(4) can be seen as a distorted variant of orthorhombic neptunium, Np, metal. Thermal expansion of KSc(BH4)(4) in the temperature range RT to 405 K is anisotropic, and the lattice parameter b shows strong nonlinearity upon approaching the melting temperature. The vibrational and NMR spectra are consistent with the structural model, and previous investigations of the related compounds ASc(BH4)(4) with A = Li, Na. KSc(BH4)(4) is stable from RT up to similar to 405 K, where the compound melts and then releases hydrogen in two rapid steps approximately at 460-500 K and 510-590 K. The hydrogen release involves the formation of KBH4, which reacts with K3ScCl6 and forms a solid solution, K(BH4)(1-x)Cl-x. The ternary potassium scandium chloride K3ScCl6 observed in all samples has a monoclinic structure at room temperature, P2(1)/a, a = 12.729(3), b = 7.367(2), c = 12.825(3) angstrom, beta = 109.22(2)degrees, V = 1135.6(4) angstrom(3), which is isostructural to K3MoCl6. The monoclinic polymorph transforms to cubic at 635 K, a = 10.694 angstrom (based on diffraction data measured at 769 K), which is isostructural to the high temperature phase of K3YCl6.

Ämnesord

NATURVETENSKAP  -- Fysik (hsv//swe)

NATURAL SCIENCES  -- Physical Sciences (hsv//eng)

Publikations- och innehållstyp

art (ämneskategori)

ref (ämneskategori)