Lateral variation of the native passive film on super duplex stainless steel resolved by synchrotron hard X-ray photoelectron emission microscopy

• A native passive film on 25Cr-7Ni super duplex stainless steel was analyzed using synchrotron hard X-ray photoemission electron microscopy, focusing on variations between individual grains of ferrite and austenite phases. The film consists of an oxide inner layer and an oxyhydroxide outer layer, in total 2.3 nm thick. The Cr content is higher in the outer than the inner layer, ca. 80 % on average. The Cr content is higher on ferrite than austenite, whereas the thickness is rather uniform. The grain orientation has a small but detectable influence, ferrite (111) grains have a lower Cr content than other ferrite grains.

Ämnesord

TEKNIK OCH TEKNOLOGIER  -- Materialteknik -- Metallurgi och metalliska material (hsv//swe)

ENGINEERING AND TECHNOLOGY  -- Materials Engineering -- Metallurgy and Metallic Materials (hsv//eng)

NATURVETENSKAP  -- Kemi -- Materialkemi (hsv//swe)

NATURAL SCIENCES  -- Chemical Sciences -- Materials Chemistry (hsv//eng)

NATURVETENSKAP  -- Kemi -- Oorganisk kemi (hsv//swe)

NATURAL SCIENCES  -- Chemical Sciences -- Inorganic Chemistry (hsv//eng)

Nyckelord

duplex stainless steel

lateral variation

passive film

photoelectron emission spectroscopy

synchrotron technique

duplex stainless steel

Kemi

Publikations- och innehållstyp

art (ämneskategori)

ref (ämneskategori)