InP nanowire p-type doping via Zinc indiffusion

• We report an alternative pathway for p-type InP nanowire (NW) doping by diffusion of Zn species from the gas phase. The diffusion of Zn was performed in a MOVPE reactor at 350–500 °C for 5–20 min with either H2 environment or additional phosphorus in the atmosphere. In addition, Zn3P2 shells were studied as protective caps during post-diffusion annealing. This post-diffusion annealing was performed to outdiffuse and activate Zn in interstitial locations. The characterization methods included photoluminescence and single NW conductivity and carrier concentration measurements. The acquired carrier concentrations were in the order of >1017 cm−3 for NWs without post-annealing, and up to 1018 cm−3 for NWs annealed with the Zn3P2 shells. The diffused Zn caused redshift to the photoluminescence signal, and the degree of redshift depended on the diffusion process.

Ämnesord

TEKNIK OCH TEKNOLOGIER  -- Nanoteknik -- Nanoteknik (hsv//swe)

ENGINEERING AND TECHNOLOGY  -- Nano-technology -- Nano-technology (hsv//eng)

NATURVETENSKAP  -- Fysik -- Den kondenserade materiens fysik (hsv//swe)

NATURAL SCIENCES  -- Physical Sciences -- Condensed Matter Physics (hsv//eng)

Nyckelord

A1. Annealing

A1. Diffusion

A1. Doping

A3. Metalorganic vapor phase epitaxy

B2. Semiconducting III–V materials

B3. Field effect transistors

Publikations- och innehållstyp

art (ämneskategori)

ref (ämneskategori)