TRANSMISSION ELECTRON-MICROSCOPY INVESTIGATION OF THE MORPHOLOGY OF INP STRANSKI-KRASTANOW ISLANDS GROWN BY METALORGANIC CHEMICAL-VAPOR-DEPOSITION
- Article/chapterEnglish1995
Publisher, publication year, extent ...
Numbers
-
LIBRIS-ID:oai:lup.lub.lu.se:cfe08f68-90f8-43f2-b4f9-aacc617eaceb
-
https://lup.lub.lu.se/record/cfe08f68-90f8-43f2-b4f9-aacc617eacebURI
-
https://doi.org/10.1063/1.114832DOI
Supplementary language notes
-
Language:English
-
Summary in:English &Swedish
Part of subdatabase
Classification
-
Subject category:art swepub-publicationtype
-
Subject category:ref swepub-contenttype
Notes
-
We have used transmission electron microscopy to determine the morphology of InP Stranski–Krastanow islands in GaInP, grown by metalorganic chemical vapor deposition at 580 °C. We investigated both capped and uncapped islands. It was found that the fully developed islands have the principal shape of truncated pyramids with a hexagonal base both before and after overgrowth. The planes defining the islands are of {001}, {110}, and {111} types. The base dimensions are 40–50 nm and 55–65 nm in the [1̄10] and [110] directions, respectively, and the height is 12–18 nm.
-
We have used transmission electron microscopy to determine the morphology of InP Stranski-Krastanow islands in GaInP, grown by metalorganic chemical vapor deposition at 580 degrees C. We investigated both capped and uncapped islands. It was found that the fully developed islands have the principal shape of truncated pyramids with a hexagonal base both before and after overgrowth. The planes defining the islands are of 001, 110, and 111 types. The base dimensions are 40-50 nm and 55-65 nm in the [(1) over bar 110] and [110] directions, respectively, and the height is 12-18 nm. (C) 1995 American Institute of Physics.
Subject headings and genre
Added entries (persons, corporate bodies, meetings, titles ...)
-
Carlsson, NLund University,Lunds universitet,Fasta tillståndets fysik,Fysiska institutionen,Institutioner vid LTH,Lunds Tekniska Högskola,Solid State Physics,Department of Physics,Departments at LTH,Faculty of Engineering, LTH(Swepub:lu)extLU-1222
(author)
-
Samuelson, LLund University,Lunds universitet,Fasta tillståndets fysik,Fysiska institutionen,Institutioner vid LTH,Lunds Tekniska Högskola,Solid State Physics,Department of Physics,Departments at LTH,Faculty of Engineering, LTH(Swepub:lu)ftf-lsa
(author)
-
Seifert, WLund University,Lunds universitet,Fasta tillståndets fysik,Fysiska institutionen,Institutioner vid LTH,Lunds Tekniska Högskola,Solid State Physics,Department of Physics,Departments at LTH,Faculty of Engineering, LTH(Swepub:lu)ftf-wse
(author)
-
Wallenberg, LRLund University,Lunds universitet,Centrum för analys och syntes,Kemiska institutionen,Institutioner vid LTH,Lunds Tekniska Högskola,Centre for Analysis and Synthesis,Department of Chemistry,Departments at LTH,Faculty of Engineering, LTH(Swepub:lu)ook2-rwa
(author)
-
Lund UniversityFasta tillståndets fysik
(creator_code:org_t)
Related titles
-
In:Applied Physics Letters: AIP Publishing67:20, s. 2981-29820003-69511077-3118
Internet link
Find in a library
To the university's database