Electron Image Series Reconstruction of Twin Interfaces in InP Superlattice Nanowires.

Ek, MartinLund University,Lunds universitet,Centrum för analys och syntes,Kemiska institutionen,Institutioner vid LTH,Lunds Tekniska Högskola,Centre for Analysis and Synthesis,Department of Chemistry,Departments at LTH,Faculty of Engineering, LTH (författare)

The twin interface structure in twinning superlattice InP nanowires with zincblende structure has been investigated using electron exit wavefunction restoration from focal series images recorded on an aberration-corrected transmission electron microscope. By comparing the exit wavefunction phase with simulations from model structures, it was possible to determine the twin structure to be the ortho type with preserved In-P bonding order across the interface. The bending of the thin nanowires away from the intended ⟨110⟩ axis could be estimated locally from the calculated diffraction pattern, and this parameter was successfully taken into account in the simulations.

Borgström, MagnusLund University,Lunds universitet,Fasta tillståndets fysik,Fysiska institutionen,Institutioner vid LTH,Lunds Tekniska Högskola,Solid State Physics,Department of Physics,Departments at LTH,Faculty of Engineering, LTH(Swepub:lu)ftf-mbo (författare)
Karlsson, LisaLund University,Lunds universitet,Centrum för analys och syntes,Kemiska institutionen,Institutioner vid LTH,Lunds Tekniska Högskola,Centre for Analysis and Synthesis,Department of Chemistry,Departments at LTH,Faculty of Engineering, LTH(Swepub:lu)mate-lka (författare)
Hetherington, CrispinLund University,Lunds universitet,Centrum för analys och syntes,Kemiska institutionen,Institutioner vid LTH,Lunds Tekniska Högskola,Centre for Analysis and Synthesis,Department of Chemistry,Departments at LTH,Faculty of Engineering, LTH(Swepub:lu)poly-cho (författare)
Wallenberg, ReineLund University,Lunds universitet,Centrum för analys och syntes,Kemiska institutionen,Institutioner vid LTH,Lunds Tekniska Högskola,Centre for Analysis and Synthesis,Department of Chemistry,Departments at LTH,Faculty of Engineering, LTH(Swepub:lu)ook2-rwa (författare)
Centrum för analys och syntesKemiska institutionen (creator_code:org_t)

Av författaren/redakt...: Ek, Martin; Borgström, Magnu ...; Karlsson, Lisa; Hetherington, Cr ...; Wallenberg, Rein ...

Om ämnet

Kungliga biblioteket hanterar dina personuppgifter i enlighet med EU:s dataskyddsförordning (2018), GDPR. Läs mer om hur det funkar här.
Så här hanterar KB dina uppgifter vid användning av denna tjänst.