We investigate a new method of coercive field engineering for periodic poling of RbKTiOPO4 (RKTP). By ion exchanging RKTP in a molten salt containing 7 mol% Ba(NO3)2 and 93 mol% KNO3 we achieve more than an order of magnitude difference in polarization switching time between the exchanged and non-exchanged regions. This method is used to fabricate periodic gratings of 2.92 µm in 1 mm thick bulk RKTP for second harmonic generation at 779 nm with a normalized conversion efficiency of 2%/Wcm. We show that the poled domain structures are stable at 300 °C, and that there is no bulk refractive index modification associated with the periodic ion exchange.

Lee, Cherrie,1992-KTH,Biomedicinsk fysik och röntgenfysik(Swepub:kth)u19az36q (författare)
Zukauskas, AndriusKTH,Laserfysik(Swepub:kth)u12rbqei (författare)
Laurell, Fredrik,professor,1957-KTH,Laserfysik(Swepub:kth)u1z0sdyv (författare)
Canalias, CarlotaKTH,Biomedicinsk fysik och röntgenfysik(Swepub:kth)u1gtitq9 (författare)
KTHLaserfysik (creator_code:org_t)

Av författaren/redakt...: Barrett, Laura; Lee, Cherrie, 19 ...; Zukauskas, Andri ...; Laurell, Fredrik ...; Canalias, Carlot ...

Om ämnet

Kungliga biblioteket hanterar dina personuppgifter i enlighet med EU:s dataskyddsförordning (2018), GDPR. Läs mer om hur det funkar här.
Så här hanterar KB dina uppgifter vid användning av denna tjänst.