Ion and solvent dynamics in gel electrolytes based on ethylene oxide grafted acrylate polymers
-
- Adebahr, J (författare)
- Chalmers tekniska högskola,Chalmers University of Technology
-
Forsyth, M (författare)
-
- Gavelin, Patrik (författare)
- Lund University,Lunds universitet,Centrum för analys och syntes,Kemiska institutionen,Institutioner vid LTH,Lunds Tekniska Högskola,Centre for Analysis and Synthesis,Department of Chemistry,Departments at LTH,Faculty of Engineering, LTH
-
visa fler...
-
- Jacobsson, Per, 1958 (författare)
- Chalmers tekniska högskola,Chalmers University of Technology
-
- Orädd, Greger (författare)
- Umeå universitet,Kemiska institutionen
-
visa färre...
-
(creator_code:org_t)
- 2002-11-01
- 2002
- Engelska.
-
Ingår i: The Journal of Physical Chemistry Part B. - : American Chemical Society (ACS). - 1520-5207 .- 1520-6106 .- 1089-5647. ; 106:47, s. 12119-12123
- Relaterad länk:
-
http://dx.doi.org/10...
-
visa fler...
-
https://lup.lub.lu.s...
-
https://doi.org/10.1...
-
https://urn.kb.se/re...
-
https://research.cha...
-
visa färre...
Abstract
Ämnesord
Stäng
- Multinuclear pulsed field gradient NMR measurements and theological viscosity measurements were performed on three series of polymer gel electrolytes. The gels were based on a lithium salt electrolyte swollen into a copolymer matrix comprising an acrylate backbone and ethylene oxide side chains. In each series the side chains differed in length and number, but the acrylate-to-ethylene oxide ratio was kept constant. It was found that the self-diffusion coefficient of the cations was much lower than that of the anions, and that it decreased rapidly when the side chains got longer. In contrast, the self-diffusion coefficient of the anions was found to be independent of chain length. In the gel electrolytes, the diffusion coefficients of the solvent molecules are relatively constant despite an increased viscosity with increasing length of the side chains. However, in saltfree gels made for comparison, the diffusion coefficients of the solvent molecules decreased with, increasing length of the side chains, which is consistent with an increased viscosity.
Ämnesord
- NATURVETENSKAP -- Kemi (hsv//swe)
- NATURAL SCIENCES -- Chemical Sciences (hsv//eng)
- TEKNIK OCH TEKNOLOGIER -- Annan teknik (hsv//swe)
- ENGINEERING AND TECHNOLOGY -- Other Engineering and Technologies (hsv//eng)
Publikations- och innehållstyp
- art (ämneskategori)
- ref (ämneskategori)
Hitta via bibliotek
Till lärosätets databas