Performance and wear mechanisms of whisker-reinforced alumina, coated and uncoated PCBN tools when high-speed turning aged Inconel 718
- Artikel/kapitelEngelska2013
Förlag, utgivningsår, omfång ...
-
2012-09-06
-
Springer Science and Business Media LLC,2013
-
electronicrdacarrier
Nummerbeteckningar
-
LIBRIS-ID:oai:lup.lub.lu.se:f5844dfc-4bcf-4044-b655-eb1d945869af
-
https://lup.lub.lu.se/record/3403710URI
-
https://doi.org/10.1007/s00170-012-4477-5DOI
Kompletterande språkuppgifter
-
Språk:engelska
-
Sammanfattning på:engelska
Ingår i deldatabas
Klassifikation
-
Ämneskategori:art swepub-publicationtype
-
Ämneskategori:ref swepub-contenttype
Anmärkningar
-
Abstract in UndeterminedInconel 718, an efficient superalloy for energy and aerospace applications, is currently machined with cemented carbide tools at low speed (vc≈60 m/min) due to its unfavorable mechanical and thermal properties. The article presents results of a study of superalloy machinability with whisker reinforced alumina, uncoated and coated PCBN tools. Turning of age hardened Inconel 718 (45 HRC) was done under high speed machining conditions (vc=250…350 m/min). Aspects of tool life, tool wear and generated surface quality were studied. Application of uncoated PCBN tools resulted in surface quality and force level superior to other tool materials. Considerable side-flow of workpiece material was found to affect surface quality, especially for coated PCBN and ceramic tools. It was found that protective function of the coating, which increases the tool life up to 20%, is limited only to low cutting speed range. EDX and AFM analyses suggested dominance of chemical and abrasive wear mechanisms. EDX mapping of worn tools pointed absence of diffusional wear for PCBN tools and intensive degradation of whisker reinforcement in ceramic tools due to diffusion of Ni, Fe and Cr.
Ämnesord och genrebeteckningar
Biuppslag (personer, institutioner, konferenser, titlar ...)
-
Zhou, JinmingLund University,Lunds universitet,Industriell Produktion,Institutionen för maskinvetenskaper,Institutioner vid LTH,Lunds Tekniska Högskola,Production and Materials Engineering,Department of Mechanical Engineering Sciences,Departments at LTH,Faculty of Engineering, LTH(Swepub:lu)mtov-jzh
(författare)
-
Avdovic, Pajazit
(författare)
-
Ståhl, Jan-EricLund University,Lunds universitet,Industriell Produktion,Institutionen för maskinvetenskaper,Institutioner vid LTH,Lunds Tekniska Högskola,Production and Materials Engineering,Department of Mechanical Engineering Sciences,Departments at LTH,Faculty of Engineering, LTH(Swepub:lu)mtov-jst
(författare)
-
Industriell ProduktionInstitutionen för maskinvetenskaper
(creator_code:org_t)
Sammanhörande titlar
-
Ingår i:International Journal of Advanced Manufacturing Technology: Springer Science and Business Media LLC66:9-12, s. 2013-20210268-37681433-3015
Internetlänk
Hitta via bibliotek
Till lärosätets databas