Pressure-induced phase transitions in α-ZrMo2O8

We report high-pressure Raman, infrared (IR), and optical-absorption spectra of α-ZrMo2O8 (trigonal) up to 38 GPa at room temperature. The spectroscopic studies are consistent with diffraction results that show that α-ZrMo2O8 transforms into δ-ZrMo2O8 (monoclinic) at about 1 GPa and the δ phase converts to the ε phase (triclinic) at about 2.0 GPa. Optical-absorption measurements give an estimate of the band gap of about 0.6 eV at the lowest pressure. Band-gap changes with pressure are confirmed with visual observations. ZrMo2O8 changes from transparent at 5 GPa to yellow at 10 GPa, red at 18 GPa, and at about 30 GPa it becomes opaque.

Chen, B.University of Missouri-Kansas City (författare)
Wrobel, J. M.University of Missouri-Kansas City (författare)
Andersen, A. M KroghUniversity of Missouri-Kansas City (författare)
Carlson, S.Lund University,Lunds universitet,MAX IV-laboratoriet,MAX IV Laboratory(Swepub:lu)inor-sca (författare)
Kruger, M. B.University of Missouri-Kansas City (författare)
University of Missouri-Kansas CityMAX IV-laboratoriet (creator_code:org_t)

Av författaren/redakt...: Muthu, D. V S; Chen, B.; Wrobel, J. M.; Andersen, A. M K ...; Carlson, S.; Kruger, M. B.

Kungliga biblioteket hanterar dina personuppgifter i enlighet med EU:s dataskyddsförordning (2018), GDPR. Läs mer om hur det funkar här.
Så här hanterar KB dina uppgifter vid användning av denna tjänst.