Cold-rolling and recrystallization textures of a nano-lamellar AlCoCrFeNi2.1 eutectic high entropy alloy

Wani, I. S. (författare)
Indian Institute of Technology
Bhattacharjee, T. (författare)
Kyoto University
Sheikh, Saad Ahmed, 1987 (författare)
Chalmers tekniska högskola,Chalmers University of Technology
visa fler...
Clark, I. T. (författare)
Park, M. H. (författare)
Kyoto University
Okawa, T. (författare)
Guo, Sheng, 1981 (författare)
Chalmers tekniska högskola,Chalmers University of Technology
Bhattacharjee, P. P. (författare)
Indian Institute of Technology
Tsuji, N. (författare)
Kyoto University
visa färre...
 (creator_code:org_t)
Elsevier BV, 2017
2017
Engelska.
Ingår i: Intermetallics. - : Elsevier BV. - 0966-9795. ; 84, s. 42-51
  • Tidskriftsartikel (refereegranskat)
Abstract Ämnesord
Stäng  
  • The development of texture during cold-rolling and recrystallization was investigated in a AlCoCrFeNi2.1 eutectic high entropy alloy (EHEA). For this purpose, the as-cast alloy was cold-rolled to 90% reduction in thickness and annealed at temperatures ranging from 800 °C to 1200 °C. The microstructure of the as-cast EHEA showed a nano-lamellar mixture of L12 and B2 phases. The B2 phase was significantly harder than the L12 phase. Development of an ultrafine microstructure was observed after 90% cold-rolling. During cold-rolling, progressive disordering of the L12 phase was observed while the B2 phase maintained the ordered structure. The progressive disordering and development of a predominantly brass type texture in the L12 phase correlated well with profuse shear band formation during cold-rolling. The B2 phase showed the presence of the {111} component which was typical for cold-rolled B2 alloys. An ultrafine duplex structure of equiaxed L12 and B2 phases developed after complete recrystallization that showed significant resistance to grain growth up to very high annealing temperatures (?1300 °C). The remarkable resistance to grain growth compared to conventional or even other single or dual phase HEAs was due to the formation of a homogeneous duplex structure where growth of one phase was effectively retarded by the other phase. The strong presence of the ?-fiber components, but weak BR ({236} ) and D ({113} ) components in the recrystallization texture of the L12/FCC phase was due to the absence of strong preferential nucleation or growth. Presence of ND-fiber (ND// ) with strong {111} component in the recrystallization texture of the B2 phase indicated ease of nucleation from similarly oriented regions in the deformed microstructure.

Ämnesord

TEKNIK OCH TEKNOLOGIER  -- Materialteknik (hsv//swe)
ENGINEERING AND TECHNOLOGY  -- Materials Engineering (hsv//eng)

Nyckelord

EBSD
Cold-rolling
Recrystallization
High entropy alloy
Texture

Publikations- och innehållstyp

art (ämneskategori)
ref (ämneskategori)

Hitta via bibliotek

Till lärosätets databas

Kungliga biblioteket hanterar dina personuppgifter i enlighet med EU:s dataskyddsförordning (2018), GDPR. Läs mer om hur det funkar här.
Så här hanterar KB dina uppgifter vid användning av denna tjänst.

 
pil uppåt Stäng

Kopiera och spara länken för att återkomma till aktuell vy