  • Di, Wei,1986Chalmers tekniska högskola,Chalmers University of Technology (författare)

CO2 hydrogenation to light olefins using In2O3 and SSZ-13 catalyst-Understanding the role of zeolite acidity in olefin production

  • Artikel/kapitelEngelska2023

Förlag, utgivningsår, omfång ...

  • 2023
  • electronicrdacarrier

Nummerbeteckningar

  • LIBRIS-ID:oai:research.chalmers.se:10409b83-2959-4d64-a47b-d54629d3d633
  • https://research.chalmers.se/publication/536552URI
  • https://doi.org/10.1016/j.jcou.2023.102512DOI

Kompletterande språkuppgifter

  • Språk:engelska
  • Sammanfattning på:engelska

Ingår i deldatabas

Klassifikation

  • Ämneskategori:art swepub-publicationtype
  • Ämneskategori:ref swepub-contenttype

Anmärkningar

  • With the aim to explore the effect of acidic properties of zeolites in tandem catalysts on their performance for CO2 hydrogenation, two types of SSZ-13 zeolites with similar bulk composition, but different arrangements of framework Al, were prepared. Their morphology, pore structure, distribution of framework Al, surface acid strength and density, were explored. The results showed that SSZ-13 zeolites with isolated aluminum distribution could be successfully synthesized, however, they contained structural defects. During calcination, the framework underwent dealumination, resulting in weaker Brønsted acidity and lower crystallinity. The morphologies were, however, well preserved. Compared with the SSZ-13 zeolites, synthesized conventionally, these low acidity SSZ13 zeolites with isolated aluminum were good zeolite components in bifunctional catalysts for CO2 hydrogenation to light olefins. By combining with In2O3, they exhibited better catalytic performance for light olefin production during CO2 hydrogenation at low temperatures. Na+ cation exchange was used to adjust the Brønsted acid site (BAS) density with only minor changes to the cavity structure. Comparative experiments established that the BAS density of the zeolite, rather than the framework Al distribution (BAS distribution), overwhelmingly affected catalyst stability and product selectivity. A higher acid density reduced the selectivity for light olefins, while lower acid density tended to form inert coke species leading to rapid deactivation. The ideal amount of BAS density in the bifunctional catalyst was approximately 0.25 mmol/g, which exhibited 70% selectivity for light olefins among hydrocarbons, and 74% selectivity for CO without deactivation, after 12 h reaction at 325 celcius and 10 bar.

Ämnesord och genrebeteckningar

Biuppslag (personer, institutioner, konferenser, titlar ...)

  • Ho, Hoang Phuoc,1983Chalmers tekniska högskola,Chalmers University of Technology(Swepub:cth)phuoc (författare)
  • Achour, Abdenour,1980Chalmers tekniska högskola,Chalmers University of Technology(Swepub:cth)abdenour (författare)
  • Pajalic, Oleg (författare)
  • Josefsson, Lars (författare)
  • Olsson, Louise,1974Chalmers tekniska högskola,Chalmers University of Technology(Swepub:cth)louisej (författare)
  • Creaser, Derek,1966Chalmers tekniska högskola,Chalmers University of Technology(Swepub:cth)creaser (författare)
  • Chalmers tekniska högskola (creator_code:org_t)

Sammanhörande titlar

  • Ingår i:Journal of CO2 Utilization722212-9820

Internetlänk

Hitta via bibliotek

Till lärosätets databas

Kungliga biblioteket hanterar dina personuppgifter i enlighet med EU:s dataskyddsförordning (2018), GDPR. Läs mer om hur det funkar här.
Så här hanterar KB dina uppgifter vid användning av denna tjänst.

 
pil uppåt Stäng

Kopiera och spara länken för att återkomma till aktuell vy