Hot cracking in cast alloy 718

• Hot cracking susceptibility of the Fe–Ni-based precipitation hardening cast superalloy Alloy 718 was studied by Varestraint weldability testing. The effect of two hot isostatic pressing (HIP) treatments commonly employed in the aerospace industry was investigated in reference to the as cast condition. It was found that the heat affected zone (HAZ) liquation cracking susceptibility increased for samples with pre-weld HIP treatments. The as cast condition disclosed the best response for liquation cracking followed by HIP-1120 (1120°C/4h (HIP) + 1050°C/1h and furnace cooling to 650°C/1h in vacuum + 950°C/1h) and HIP-1190 (1190°C/4h (HIP) + 870°C/10h and furnace cooling to 650°C/1h in vacuum + 950°C/1h). The amount of the secondary precipitates and base metal grain size was found to be important parameters influencing the cracking susceptibility. Regarding solidification cracking susceptibility, the three conditions appear to behave similarly.

Ämnesord

TEKNIK OCH TEKNOLOGIER  -- Materialteknik -- Bearbetnings-, yt- och fogningsteknik (hsv//swe)

ENGINEERING AND TECHNOLOGY  -- Materials Engineering -- Manufacturing, Surface and Joining Technology (hsv//eng)

TEKNIK OCH TEKNOLOGIER  -- Materialteknik -- Metallurgi och metalliska material (hsv//swe)

ENGINEERING AND TECHNOLOGY  -- Materials Engineering -- Metallurgy and Metallic Materials (hsv//eng)

Nyckelord

Hot cracking

solidification cracking

Varestraint testing

alloy 718

liquation cracking

hot isostatic pressing

Manufacturing and materials engineering

Publikations- och innehållstyp

art (ämneskategori)

ref (ämneskategori)