Esmaily, Mohsen,1987Chalmers tekniska högskola,Chalmers University of Technology (författare)

In this study, ultra-fine grained (UFG) structure was produced in the stir zone (SZ) of AA6005-T6 alloy joints using friction stir processing (FSP) cooled by liquid nitrogen (N 2 ). Conventional friction stir welding (FSW) was used to fabricate reference joints. The corrosion properties of the cooled joints were investigated by atmospheric corrosion tests. The corrosion exposures were carried out at a relative humidity (RH) of 95%, 400 ppm CO 2 and at 22°C. The rapidly cooled joints exhibited exceptional corrosion resistance in both corrosion experiments as well as better mechanical properties compared to those of the FSWed joints. The better corrosion resistance of the quenched sample was attributed to the microstructural modification of the joint.

Blucher, D. B.SINTEF Materials and Chemistry (författare)
Svensson, Jan-Erik,1965Chalmers tekniska högskola,Chalmers University of Technology(Swepub:cth)jes (författare)
Halvarsson, M.SINTEF Materials and Chemistry (författare)
Johansson, Lars-Gunnar,1952Chalmers tekniska högskola,Chalmers University of Technology(Swepub:cth)lg (författare)
Chalmers tekniska högskolaSINTEF Materials and Chemistry (creator_code:org_t)

Ingår i:ECS Transactions: The Electrochemical Society64:26, s. 29-431938-58621938-6737

Av författaren/redakt...: Esmaily, Mohsen, ...; Blucher, D. B.; Svensson, Jan-Er ...; Halvarsson, M.; Johansson, Lars- ...

Om ämnet

TEKNIK OCH TEKNOLOGIER: TEKNIK OCH TEKNO ...; och Materialteknik; och Metallurgi och m ...

TEKNIK OCH TEKNOLOGIER: TEKNIK OCH TEKNO ...; och Kemiteknik; och Korrosionsteknik

Kungliga biblioteket hanterar dina personuppgifter i enlighet med EU:s dataskyddsförordning (2018), GDPR. Läs mer om hur det funkar här.
Så här hanterar KB dina uppgifter vid användning av denna tjänst.