  • Mauri, Massimiliano,1987Chalmers tekniska högskola,Chalmers University of Technology (författare)

Click chemistry-type crosslinking of a low-conductivity polyethylene copolymer ternary blend for power cable insulation

  • Artikel/kapitelEngelska2020

Förlag, utgivningsår, omfång ...

  • 2020-02-03
  • Wiley,2020

Nummerbeteckningar

  • LIBRIS-ID:oai:research.chalmers.se:183ec3e9-6fa9-47ae-936e-2f67d2d688a6
  • https://research.chalmers.se/publication/515414URI
  • https://doi.org/10.1002/pi.5966DOI

Kompletterande språkuppgifter

  • Språk:engelska
  • Sammanfattning på:engelska

Ingår i deldatabas

Klassifikation

  • Ämneskategori:art swepub-publicationtype
  • Ämneskategori:ref swepub-contenttype

Anmärkningar

  • High-voltage direct-current power cables are vital for the efficient transport of electricity derived from renewable sources of energy. The most widely used material for high-voltage power cable insulation - low-density polyethylene (LDPE) - is usually crosslinked with peroxides, a process that releases unwanted by-products. Hence, by-product-free crosslinking concepts that mitigate the associated increase in electrical conductivity are in high demand. Click chemistry-type crosslinking of polyethylene copolymer mixtures that contain glycidyl methacrylate and acrylic acid co-monomers is a promising alternative, provided that the curing reaction can be controlled. Here, we demonstrate that the rate of the curing reaction can be adjusted by tuning the number of epoxy and carboxyl groups. Both dilution of copolymer mixtures with neat LDPE and the selection of copolymers with a lower co-monomer content have an equivalent effect on the curing speed. Ternary blends that contain 50 wt% of neat LDPE feature an extended extrusion window of up to 170 degrees C. Instead, at 200 degrees C rapid curing is possible, leading to thermosets with a low direct-current electrical conductivity of about 10(-16) S cm(-1) at an electric field of 20 kV mm(-1) and 70 degrees C. The conductivity of the blends explored here is comparable to or even lower than values measured for both ultraclean LDPE and a peroxide-cured commercial crosslinked polyethylene grade. Hence, click chemistry curing represents a promising alternative to radical crosslinking with peroxides. (c) 2019 Society of Chemical Industry

Ämnesord och genrebeteckningar

Biuppslag (personer, institutioner, konferenser, titlar ...)

  • Hofmann, Anna,1987Chalmers tekniska högskola,Chalmers University of Technology(Swepub:cth)hofanna (författare)
  • Gomez-Heincke, DianaBorealis GmbH (författare)
  • Kumara, Sarath,1979Chalmers tekniska högskola,Chalmers University of Technology(Swepub:cth)sarath (författare)
  • Pourrahimi, Amir Masoud,1985Chalmers tekniska högskola,Chalmers University of Technology(Swepub:cth)amirmas (författare)
  • Ouyang, Yingwei,1995Chalmers tekniska högskola,Chalmers University of Technology(Swepub:cth)yingwei (författare)
  • Hagstrand, Per-OlaBorealis GmbH (författare)
  • Gkourmpis, ThomasBorealis GmbH (författare)
  • Xu, Xiangdong,1984Chalmers tekniska högskola,Chalmers University of Technology(Swepub:cth)xiangdon (författare)
  • Prieto, OscarBorealis GmbH (författare)
  • Müller, Christian,1980Chalmers tekniska högskola,Chalmers University of Technology(Swepub:cth)cmuller (författare)
  • Chalmers tekniska högskolaBorealis GmbH (creator_code:org_t)

Sammanhörande titlar

  • Ingår i:Polymer International: Wiley69:4, s. 404-4121097-01260959-8103

Internetlänk

Hitta via bibliotek

Till lärosätets databas

Kungliga biblioteket hanterar dina personuppgifter i enlighet med EU:s dataskyddsförordning (2018), GDPR. Läs mer om hur det funkar här.
Så här hanterar KB dina uppgifter vid användning av denna tjänst.

 
pil uppåt Stäng

Kopiera och spara länken för att återkomma till aktuell vy