Oxidation of iron at 400-600 °C in dry and wet O2

Pujilaksono, Bagas,1965Chalmers tekniska högskola,Chalmers University of Technology (författare)

The oxidation of iron in dry and wet O-2 at 400-600 degrees C has been re-investigated using gravimetry, SEM/EDX, XRD and FIB. In the presence of O-2, water vapour accelerates iron oxidation at 500 and 600 degrees C. At 400 and 500 degrees C the magnetite layer is duplex and exposure to water vapour results in the formation of blades on top of a fine-grained hematite layer. At 600 degrees C it results in a surface without needles and blades. The increased oxidation rate at 500 and 600 degrees C is attributed to a smaller grain size in the hematite layer resulting in faster ion transport.

Jonsson, Torbjörn,1970Chalmers tekniska högskola,Chalmers University of Technology(Swepub:cth)tj (författare)
Halvarsson, Mats,1965Chalmers tekniska högskola,Chalmers University of Technology(Swepub:cth)f10mh (författare)
Svensson, Jan-Erik,1965Chalmers tekniska högskola,Chalmers University of Technology(Swepub:cth)jes (författare)
Johansson, Lars-Gunnar,1952Chalmers tekniska högskola,Chalmers University of Technology(Swepub:cth)lg (författare)
Chalmers tekniska högskola (creator_code:org_t)

Av författaren/redakt...: Pujilaksono, Bag ...; Jonsson, Torbjör ...; Halvarsson, Mats ...; Svensson, Jan-Er ...; Johansson, Lars- ...

Om ämnet

Kungliga biblioteket hanterar dina personuppgifter i enlighet med EU:s dataskyddsförordning (2018), GDPR. Läs mer om hur det funkar här.
Så här hanterar KB dina uppgifter vid användning av denna tjänst.