  • Forsgren, Lilian,1990Chalmers tekniska högskola,Chalmers University of Technology (författare)

Processing and properties of thermoplastic composites containing cellulose nanocrystals or wood-based cellulose fibres

  • BokEngelska2020

Förlag, utgivningsår, omfång ...

  • Gothenburg,2020
  • electronicrdacarrier

Nummerbeteckningar

  • LIBRIS-ID:oai:research.chalmers.se:27b83189-4632-476e-a078-708f3421ab52
  • ISBN:9789179053963
  • https://research.chalmers.se/publication/519943URI

Kompletterande språkuppgifter

  • Språk:engelska
  • Sammanfattning på:engelska

Ingår i deldatabas

Klassifikation

  • Ämneskategori:dok swepub-publicationtype
  • Ämneskategori:vet swepub-contenttype

Anmärkningar

  • Cellulose nanocrystals (CNC) were surface modified with dialkylamines to increase the compatibility between the CNC and the polymeric matrix, and promising results were obtained, with a 300 % stiffness increase when the mixed dispersion was compression moulded on a laboratory scale. The manufacturing process was up-scaled using water-assisted mixing in a twin-screw extruder (TSE) followed by a second compounding step and injection moulding (IM). The composites were successfully produced using conventional melt-processing techniques but these did not show the same improvement in mechanical performance, probably due to the formation of CNC aggregates. There were indications of network formation when CNC was added, especially in the case of surface-modified CNC. Cellulose fibres and thermomechanical pulp were used as reinforcement in similar types of polymer matrices and the mixtures were similarly processed by TSE and IM. These materials were characterized with regard to appearance and durability. The discoloration of the composites due to excessive heat during processing did not significantly affect their mechanical properties, and the addition of the cellulose-based reinforcement to the polymer did not reduce its resistance to thermo-oxidative degradation compared to that of the pure matrix. In fact, the resistance to degradation was increased when lignin was present in the reinforcing element, showing a synergistic effect together with the added anti-oxidant. Superior properties were expected for the CNC composites compared to those of the larger cellulose fibre reinforcements, but in continuous production the stiffening effects were similar regardless of reinforcement type. These results confirm that the processing method and properties strongly affect the final properties of the composite.

Ämnesord och genrebeteckningar

Biuppslag (personer, institutioner, konferenser, titlar ...)

  • Chalmers tekniska högskola (creator_code:org_t)

Internetlänk

Hitta via bibliotek

Till lärosätets databas

Hitta mer i SwePub

Av författaren/redakt...
Forsgren, Lilian ...
Om ämnet
TEKNIK OCH TEKNOLOGIER
TEKNIK OCH TEKNO ...
och Materialteknik
TEKNIK OCH TEKNOLOGIER
TEKNIK OCH TEKNO ...
och Materialteknik
och Pappers massa oc ...
TEKNIK OCH TEKNOLOGIER
TEKNIK OCH TEKNO ...
och Materialteknik
och Bearbetnings yt ...
TEKNIK OCH TEKNOLOGIER
TEKNIK OCH TEKNO ...
och Materialteknik
och Kompositmaterial ...
Av lärosätet
Chalmers tekniska högskola

Sök utanför SwePub

Kungliga biblioteket hanterar dina personuppgifter i enlighet med EU:s dataskyddsförordning (2018), GDPR. Läs mer om hur det funkar här.
Så här hanterar KB dina uppgifter vid användning av denna tjänst.

 
pil uppåt Stäng

Kopiera och spara länken för att återkomma till aktuell vy