Proton conduction in Perovskite Oxide BaZr0.5Yb0.5O3-δ Prepared by Wet Chemical Route

• A wet chemical route has been used to synthesize the oxygen deficient perovskite Ba Zr0.5 Yb0.5 O3-δ. Analysis of X-ray powder diffraction data showed that both dried and hydrated samples adopt cubic crystal structures of space group Pm 3- m. Dynamic thermogravimetric analysis showed a significant mass loss for the hydrated sample compared to the dried sample, indicating that ∼28% of the oxygen vacancies are filled by protonic defects. The strong O-H stretch band, 2500-3500 cm-1, in the IR absorbance spectrum also clearly manifests the presence of significant levels of protons in the hydrated material. Proton conductivity was investigated on prehydrated (under dry Ar) and as-prepared (under wet Ar) samples. The heating cycle of the prehydrated sample showed higher proton conductivity compared to the cooling cycle, especially in the intermediate temperature range (150-550°C). Finally, comparison with data for Ba Zr0.9 Yb0.1 O3-δ revealed that the more heavily doped sample showed higher proton conductivity compared to the more lightly doped sample. © 2008 The Electrochemical Society.

Subject headings

TEKNIK OCH TEKNOLOGIER  -- Materialteknik (hsv//swe)

ENGINEERING AND TECHNOLOGY  -- Materials Engineering (hsv//eng)

TEKNIK OCH TEKNOLOGIER  -- Materialteknik -- Annan materialteknik (hsv//swe)

ENGINEERING AND TECHNOLOGY  -- Materials Engineering -- Other Materials Engineering (hsv//eng)

NATURVETENSKAP  -- Kemi (hsv//swe)

NATURAL SCIENCES  -- Chemical Sciences (hsv//eng)

Publication and Content Type

art (subject category)

ref (subject category)