Electrical and complex dielectric behaviour of composite polymer electrolyte based on PEO, alumina and tetrapropylammonium iodide

Bandara, T M W J, 1968 (författare)
Chalmers tekniska högskola,Chalmers University of Technology
Karunathilaka, D.G.N. (författare)
University of Peradeniya
Ratnasekera, J.L. (författare)
University of Colombo
visa fler...
Ajith de Silva, L. (författare)
University of West Georgia
Herath, A.C. (författare)
University of Colombo
Mellander, Bengt-Erik, 1949 (författare)
Chalmers tekniska högskola,Chalmers University of Technology
visa färre...
 (creator_code:org_t)
2017-02-24
2017
Engelska.
Ingår i: Ionics. - : Springer Science and Business Media LLC. - 0947-7047 .- 1862-0760. ; 23:7, s. 1711-1719
  • Tidskriftsartikel (refereegranskat)
Abstract Ämnesord
Stäng  
  • In this study, the electrical, dielectric and morphological analysis of composite solid polymer electrolytes containing polyethylene oxide, alumina nano-fillers and tetrapropylammonium iodide are conducted. The temperature dependence of conductivity shows activation energy of 0.23, 0.20 and 0.29 eV for electrolytes containing 0, 5 and 15 wt.% alumina, respectively, when data fitted to the Arrhenius equation. These activation energy values are in good agreement with those determined from dielectric measurements. The result confirms the fact that conductivity is activated by both the mobility and the charge carrier density. The conductivity isotherms demonstrated the existence of two peaks, at 5 and 15 wt.% Al2O3 composition. The highest conductivity values of 2.4 × 10−4, 3.3 × 10−4 and 4.2 × 10−4 S cm−1 are obtained for the sample with 5 wt.% Al2O3 at 0, 12 and 24 °C, respectively, suggesting an enhancement of conductivity compared with that of alumina free samples.

Ämnesord

NATURVETENSKAP  -- Fysik (hsv//swe)
NATURAL SCIENCES  -- Physical Sciences (hsv//eng)

Nyckelord

Anion conductivity
Composite polymer electrolyte
Alumina nano-fillers
Activation energy
Dielectric analysis

Publikations- och innehållstyp

art (ämneskategori)
ref (ämneskategori)

Hitta via bibliotek

  • Ionics (Sök värdpublikationen i LIBRIS)

Till lärosätets databas

Sök utanför SwePub

Kungliga biblioteket hanterar dina personuppgifter i enlighet med EU:s dataskyddsförordning (2018), GDPR. Läs mer om hur det funkar här.
Så här hanterar KB dina uppgifter vid användning av denna tjänst.

 
pil uppåt Stäng

Kopiera och spara länken för att återkomma till aktuell vy