Abstract
Ämnesord
Stäng
- Photoluminescent NaYF4:Yb3+/Tm3+ nanocrystals are ideally suited for in vitro and in vivo photoluminescence (PL) bioimaging due to their virtue of near-infrared to near-infrared (NIR-to-NIR) upconversion (UC); they display PL with a peak at similar to 800 nm if excited at similar to 980 nm. Here, we report the synthesis of monodisperse NaYF4:Yb3+/Tm3+ nanocrystals of ultrasmall size (7-10 nm) with high UC efficiency. The intensity of their NIR UC emission was demonstrated to increase by up to 43 times along with an increase in the relative content of Yb3+ ions from 20 to 100%, with a corresponding decrease in the Y3+ content from 80 to 0%. The achieved ultrasmall NaYbF4:2% Tm3+ nanocrystals manifest NIR PL emission, which is 3.6 times more intense than that from 25-30 nm sized NaYF4:20% Yb3+/2% Tm3+ nanocrystals, previously synthesized and used for in vitro and in vivo bioimaging. An optimization of both size and UC PL efficiency of NIR-to-NIR nanocrystals provides us with highly efficient optical imaging probes for bioapplications.
Ämnesord
- NATURVETENSKAP -- Kemi (hsv//swe)
- NATURAL SCIENCES -- Chemical Sciences (hsv//eng)
Nyckelord
- near-infrared
- upconversion photoluminescence
- nanocrystals
- rare-earth ions
- Chemistry
- Kemi
Publikations- och innehållstyp
- ref (ämneskategori)
- art (ämneskategori)
Hitta via bibliotek
-
ACS NANO
(Sök värdpublikationen i LIBRIS)
Till lärosätets databas