The initial effect ...
The initial effect of KCl deposit on alumina scales characterized by ToF-SIMS and AES
-
- Engkvist, Josefin, 1972 (författare)
- Högskolan Dalarna,Materialvetenskap,Chalmers University of Technology, Göteborg, Sweden
-
- Israelsson, Niklas, 1983 (författare)
- Chalmers tekniska högskola,Chalmers University of Technology,Chalmers University of Technology, Göteborg, Sweden
-
- Bexell, Ulf (författare)
- Högskolan Dalarna,Materialteknik
-
(creator_code:org_t)
- 2012-06-19
- 2013
- Engelska.
-
Ingår i: Surface and Interface Analysis. - : Wiley. - 1096-9918 .- 0142-2421. ; 45:1, s. 445-448
- Relaterad länk:
-
http://dx.doi.org/10...
-
visa fler...
-
https://doi.org/10.1...
-
https://research.cha...
-
https://urn.kb.se/re...
-
visa färre...
Abstract
Ämnesord
Stäng
- A FeCrAl alloy was preoxidized to form a protective alumina scale, and the effect of KCl deposits on the alumina scale was investigated while exposed during 1 and 24 h at 600 degrees C. However, impurity concentrations in the alumina scale change the ion conductivity and hence affect its protective properties. Therefore, Auger electron spectroscopy and time-of-flight secondary ion mass spectrometry were used to characterize the alumina scales and detect traces of K and Cl. The results showed that K and Cl existed as large sharp-edged crystals surrounded by a dendritic network after 1 h. However, after 24 h, those were dissolved, and K together with Cl was detected only in the outer layer of the duplex alumina scale, which was formed during preoxidation.
Ämnesord
- TEKNIK OCH TEKNOLOGIER -- Kemiteknik (hsv//swe)
- ENGINEERING AND TECHNOLOGY -- Chemical Engineering (hsv//eng)
- TEKNIK OCH TEKNOLOGIER -- Kemiteknik -- Korrosionsteknik (hsv//swe)
- ENGINEERING AND TECHNOLOGY -- Chemical Engineering -- Corrosion Engineering (hsv//eng)
Nyckelord
- Alumina
- initial oxidation
- KCl
- dry
- FeCrAl
- oxidation
- SIMS
- AES
- alloy
- o-2
- Steel Forming and Surface Engineering
Publikations- och innehållstyp
- art (ämneskategori)
- ref (ämneskategori)
Hitta via bibliotek
Till lärosätets databas