The effect of hydrogen on the breakdown of the protective oxide scale in solid oxide fuel cell interconnects

• In this study, the effect of hydrogen, on the degradation of AISI 441 interconnect, under solid oxide fuel cell operating conditions was investigated between 500−800 °C for 336 h. As a new hypothesis, it is concluded that, hydrogen impedes Cr diffusion, probably in the grain boundaries, leading to the breakdown of the protective oxide scale. This effect is most severe at 600 °C, while at lower or higher temperatures the effect is attenuated. Cr diffusion is enhanced at high temperatures, whereas protective scales can be obtained at low temperatures with a lower amount of Cr.

Ämnesord

TEKNIK OCH TEKNOLOGIER  -- Materialteknik -- Keramteknik (hsv//swe)

ENGINEERING AND TECHNOLOGY  -- Materials Engineering -- Ceramics (hsv//eng)

TEKNIK OCH TEKNOLOGIER  -- Kemiteknik -- Kemiska processer (hsv//swe)

ENGINEERING AND TECHNOLOGY  -- Chemical Engineering -- Chemical Process Engineering (hsv//eng)

TEKNIK OCH TEKNOLOGIER  -- Kemiteknik -- Annan kemiteknik (hsv//swe)

ENGINEERING AND TECHNOLOGY  -- Chemical Engineering -- Other Chemical Engineering (hsv//eng)

Nyckelord

Solid oxide fuel cell

Interconnect

Hydrogen

Corrosion

AISI 441

Dual

Atmosphere

Publikations- och innehållstyp

art (ämneskategori)

ref (ämneskategori)