Contactless Electroreflectance, Photoluminescence and Time-Resolved Photoluminescence of GaInNAs Quantum Wells Obtained by the MBE Method with N-irradiation
-
- Baranowski, M (author)
- Politechnika Wrocławska,Wrocław University of Science and Technology
-
- Kudrawiec, R (author)
- Politechnika Wrocławska,Wrocław University of Science and Technology
-
- Syperek, M (author)
- Politechnika Wrocławska,Wrocław University of Science and Technology
-
show more...
-
- Misiewicz, J (author)
- Politechnika Wrocławska,Wrocław University of Science and Technology
-
- Zhao Ternehäll, Huan, 1982 (author)
- Chalmers tekniska högskola,Chalmers University of Technology
-
- Sadeghi, Mahdad, 1964 (author)
- Chalmers tekniska högskola,Chalmers University of Technology
-
- Wang, Shu Min, 1963 (author)
- Chalmers tekniska högskola,Chalmers University of Technology
-
show less...
-
(creator_code:org_t)
- 2011-02-25
- 2011
- English.
-
In: Semiconductor Science and Technology. - : IOP Publishing. - 1361-6641 .- 0268-1242. ; 26:4, s. 045012-
- Related links:
-
http://dx.doi.org/10...
-
show more...
-
https://research.cha...
-
https://doi.org/10.1...
-
show less...
Abstract
Subject headings
Close
- The optical properties of GaInNAs quantum wells (QW) grown by molecular beam epitaxywith and without N-irradiation (i.e. grown by the classical method) were investigated by thecontactless electroreflectance (CER), temperature-dependent photoluminescence (PL) andtime-resolved PL (TRPL). From CER measurements it was concluded that one type ofnitrogen nearest-neighbor environment (In-rich environment) is dominant for GaInNAs QWsgrown with N-irradiation whereas various nitrogen environments are present for the referenceGaInNAs QW (i.e. the sample obtained by the classical method). PL and TRPL measurementsclearly show that the optical properties of GaInNAs QWs are affected mainly by the amount ofthe incorporated nitride atoms. It was observed that the PL decay time decreased from ∼200to ∼40 ps when the nitrogen concentration is increased from 0.8 to 2.2%. In addition, thepresence of As flux during N-irradiation reduces the amount of the incorporated nitrogen andsimultaneously improves the optical quality of GaInNAs QWs (i.e. it weakens the carrierlocalization at low temperatures and improves the quantum efficiency of PL).
Subject headings
- TEKNIK OCH TEKNOLOGIER -- Elektroteknik och elektronik (hsv//swe)
- ENGINEERING AND TECHNOLOGY -- Electrical Engineering, Electronic Engineering, Information Engineering (hsv//eng)
Publication and Content Type
- art (subject category)
- ref (subject category)
Find in a library
To the university's database