A comparative study on microstructure, nanomechanical and corrosion behaviors of AlCoCuFeNi high entropy alloys fabricated by selective laser melting and laser metal deposition

• The present study investigated the microstructure, nanomechanics, and corrosion behavior of AlCoCuFeNi high entropy alloys fabricated by selective laser melting (SLM) and laser metal deposition (LMD). The microstructure of SLM-processed specimens was mainly composed of columnar-grained BCC matrix (∼90 µm in width) and Cu-rich twinned FCC phase. The columnar grains grew epitaxially along the building direction and exhibited a strong {001} texture. In comparison, a coarse columnar-grained BCC matrix (∼150 µm in width) with a stronger 〈001〉 texture, rod-like B2 precipitates, and large core-shell structured FCC phases were formed in the LMD-processed specimens due to the higher heat accumulation effect. Consequently, the LMD-processed specimens showed a lower hardness, wear resistance, and corrosion resistance, but higher creep resistance and reduced Young's modulus than the SLM-processed specimens. Hot cracks occurred in both types of specimens, which could not be completely suppressed due to Cu segregation.

Subject headings

TEKNIK OCH TEKNOLOGIER  -- Materialteknik -- Bearbetnings-, yt- och fogningsteknik (hsv//swe)

ENGINEERING AND TECHNOLOGY  -- Materials Engineering -- Manufacturing, Surface and Joining Technology (hsv//eng)

TEKNIK OCH TEKNOLOGIER  -- Materialteknik -- Metallurgi och metalliska material (hsv//swe)

ENGINEERING AND TECHNOLOGY  -- Materials Engineering -- Metallurgy and Metallic Materials (hsv//eng)

TEKNIK OCH TEKNOLOGIER  -- Kemiteknik -- Korrosionsteknik (hsv//swe)

ENGINEERING AND TECHNOLOGY  -- Chemical Engineering -- Corrosion Engineering (hsv//eng)

Keyword

High entropy alloys

Nanomechanics

Selective laser melting

Corrosion

Laser metal deposition

Publication and Content Type

art (subject category)

ref (subject category)