Microstructural Investigation of the Initial Oxidation of the FeCrAlRE Alloy Kanthal AF in Dry and Wet O-2 at 600 and 800 degrees C
-
- Canovic, Sead, 1979 (författare)
- Chalmers tekniska högskola,Chalmers University of Technology
-
- Engkvist, Josefin, 1972 (författare)
- Högskolan i Dalarna,Dalarna university
-
- Liu, Fang, 1975 (författare)
- Chalmers tekniska högskola,Chalmers University of Technology
-
visa fler...
-
- Lai, Haiping, 1979 (författare)
- Chalmers tekniska högskola,Chalmers University of Technology
-
- Götlind, Helena, 1978 (författare)
- Chalmers tekniska högskola,Chalmers University of Technology
-
- Hellström, Kristina M, 1971 (författare)
- Chalmers tekniska högskola,Chalmers University of Technology
-
- Svensson, Jan-Erik, 1965 (författare)
- Chalmers tekniska högskola,Chalmers University of Technology
-
- Johansson, Lars-Gunnar, 1952 (författare)
- Chalmers tekniska högskola,Chalmers University of Technology
-
- Olsson, M. (författare)
- Högskolan i Dalarna,Dalarna university
-
- Halvarsson, Mats, 1965 (författare)
- Chalmers tekniska högskola,Chalmers University of Technology
-
visa färre...
-
(creator_code:org_t)
- The Electrochemical Society, 2010
- 2010
- Engelska.
-
Ingår i: Journal of the Electrochemical Society. - : The Electrochemical Society. - 1945-7111 .- 0013-4651. ; 157:6, s. C223-C230
- Relaterad länk:
-
http://dx.doi.org/10...
-
visa fler...
-
https://doi.org/10.1...
-
https://research.cha...
-
visa färre...
Abstract
Ämnesord
Stäng
- The FeCrAlRE (where RE is reactive element) alloy Kanthal AF was exposed isothermally at 600 and 800 degrees C for 72 h in dry O-2 and in O-2 with 10 vol % H2O. The mass gains were 3-5 times higher at the higher temperature. The presence of water vapor increased the oxidation rate at 800 degrees C, while no significant effect was observed at 600 degrees C. A thin two-layered oxide formed at 600 degrees C: an outer (Fe, Cr)(2)O-3 corundum-type oxide, containing some Al, and an inner, probably amorphous, Al-rich oxide. At 800 degrees C a two-layered oxide formed in both environments. The inner layer consisted of inward grown alpha-Al2O3. In dry O-2 the originally formed outward grown gamma-Al2O3 had transformed to alpha-Al2O3 after 72 h. Water vapor stabilized the outward grown gamma-Al2O3 and hence no transformation occurred after 72 h in humid environment. RE-rich oxide particles with varying composition (Y, Zr, and Ti) were distributed in the base oxide at both temperatures and in both environments. The RE-rich particles were separated from the alloy substrate by a layer of Al-rich oxide. At 800 degrees C the Y-rich RE particles were surrounded by thick oxide patches in both dry and humid O-2.
Ämnesord
- NATURVETENSKAP -- Kemi -- Oorganisk kemi (hsv//swe)
- NATURAL SCIENCES -- Chemical Sciences -- Inorganic Chemistry (hsv//eng)
- TEKNIK OCH TEKNOLOGIER -- Kemiteknik (hsv//swe)
- ENGINEERING AND TECHNOLOGY -- Chemical Engineering (hsv//eng)
Nyckelord
- 40-percent h2o
- 900 degrees-c
- mg-incorporation
- oxide scales
- water-vapor
- alumina scales
- cyclic oxidation
- fecraire alloys
- high-temperature oxidation
- growth
Publikations- och innehållstyp
- art (ämneskategori)
- ref (ämneskategori)
Hitta via bibliotek
Till lärosätets databas
- Av författaren/redakt...
-
Canovic, Sead, 1 ...
-
Engkvist, Josefi ...
-
Liu, Fang, 1975
-
Lai, Haiping, 19 ...
-
Götlind, Helena, ...
-
Hellström, Krist ...
-
visa fler...
-
Svensson, Jan-Er ...
-
Johansson, Lars- ...
-
Olsson, M.
-
Halvarsson, Mats ...
-
visa färre...
- Om ämnet
-
- NATURVETENSKAP
-
NATURVETENSKAP
-
och Kemi
-
och Oorganisk kemi
-
- TEKNIK OCH TEKNOLOGIER
-
TEKNIK OCH TEKNO ...
-
och Kemiteknik
- Artiklar i publikationen
-
Journal of the E ...
- Av lärosätet
-
Chalmers tekniska högskola