Charge densities at...
Abstract
Subject headings
Close
- It is found that Si/Si and Si/SiO2 interfaces exhibit different interface charge properties when bonded at comparable temperatures and surface treatments. Thermally grown oxides were bonded to bare silicon surfaces and the bonded Si/SiO2 interface was investigated on MOS-structures by the C-V technique. Interfaces prepared at temperatures in the range 900-1100°c exhibited U-shaped interface state densities. Si/Si samples were prepared using a hydrophilizing surface treatment before wafer bonding. At the same annealing temperatures, the interface state densities of the bonded Si/Si interfaces were in the range 1011-1013 cm-2 eV-1. Si/Si interfaces are found to be very sensitive to prebond chemical treatment, while Si/SiO2 interfaces are not. Native oxides at bonded silicon interfaces have a more pronounced influence on Si/Si interfaces than on Si/SiO2 interfaces
Subject headings
- TEKNIK OCH TEKNOLOGIER -- Elektroteknik och elektronik -- Annan elektroteknik och elektronik (hsv//swe)
- ENGINEERING AND TECHNOLOGY -- Electrical Engineering, Electronic Engineering, Information Engineering -- Other Electrical Engineering, Electronic Engineering, Information Engineering (hsv//eng)
Keyword
- semiconductor technology
- silicon
- interface electron states
- surface treatment
- semiconductor junctions
- elemental semiconductors
- semiconductor-insulator boundaries