Correlating Oxygen Electrode Degradation to Cr Vaporization from Metallic Interconnects in Solid Oxide Cell Stacks

Talic, BelmaSintef Foundation for Scientific and Industrial Research At the Norwegian Institute of Technology,Danmarks Tekniske Universitet,Technical University of Denmark (författare)

Symmetrical cells consisting of La0.58Sr0.4Co0.2Fe0.8O3-δ (LSCF) oxygen electrodes screen printed on both sides of a Ce0.9Gd0.1O2-δ (CGO) electrolyte were tested at 800 °C while being held close to a piece of Crofer 22 APU alloy. The alloy was either just pre-oxidized or coated with MnCo2O4 and heat treated prior to the exposure test to elucidate the effects of different Cr vaporization rates. Degradation of the symmetrical cells was monitored by electrochemical impedance spectroscopy, and TOF-SIMS, SEM and EDX analysis were used to examine Cr deposition on the electrodes after the exposure. The results show that the degradation rate of the symmetrical cell is directly proportional to the concentration of gaseous Cr(VI)-species, which had been assessed in a previous experiment. The Cr vaporization rate from Crofer 22 APU with a dense MnCo2O4 coating was measured in moisturized air up with up to 40% H2O and found to be invariant with respect to the steam activity. The degradation rate of symmetrical cells was accelerated by humidity in the air, but, noteworthy, this was found also in the absence of a Cr source.

Norrman, K.King Fahd University of Petroleum and Minerals (författare)
Sand, Tommy,1982Chalmers tekniska högskola,Chalmers University of Technology(Swepub:cth)satommy (författare)
Froitzheim, Jan,1981Chalmers tekniska högskola,Chalmers University of Technology(Swepub:cth)froitzhe (författare)
Hendriksen, Peter VangDanmarks Tekniske Universitet,Technical University of Denmark (författare)
Sintef Foundation for Scientific and Industrial Research At the Norwegian Institute of TechnologyDanmarks Tekniske Universitet (creator_code:org_t)

Av författaren/redakt...: Talic, Belma; Norrman, K.; Sand, Tommy, 198 ...; Froitzheim, Jan, ...; Hendriksen, Pete ...

Om ämnet

TEKNIK OCH TEKNOLOGIER: TEKNIK OCH TEKNO ...; och Kemiteknik; och Annan kemiteknik

Kungliga biblioteket hanterar dina personuppgifter i enlighet med EU:s dataskyddsförordning (2018), GDPR. Läs mer om hur det funkar här.
Så här hanterar KB dina uppgifter vid användning av denna tjänst.