Baghdadchi, Amir,1994-Högskolan Väst,Avdelningen för svetsteknologi (SV),KAMPT
(author)
Ductilization and grain refinement of AA7075-T651 alloy via stationary shoulder friction stir processing
- Article/chapterEnglish2023
Publisher, publication year, extent ...
-
2023
-
electronicrdacarrier
Numbers
-
LIBRIS-ID:oai:DiVA.org:hv-21002
-
https://urn.kb.se/resolve?urn=urn:nbn:se:hv:diva-21002URI
-
https://doi.org/10.1016/j.jmrt.2023.11.041DOI
Supplementary language notes
-
Language:English
-
Summary in:English
Part of subdatabase
Classification
-
Subject category:ref swepub-contenttype
-
Subject category:art swepub-publicationtype
Notes
-
CC-BY 4.0The authors would like to thank for the financial support from the funded project by Postdoctoral Science Foundation China [2019M663815].
-
This study investigates the microstructural evolution, mechanical properties, and fracture behavior of AA7075-T651 aluminium alloy subjected to stationary shoulder friction stir processing (SSFSP). SSFSP samples were produced at three different rotational speeds in a range of 600–1000 rpm. The results reveal that SSFSP leads to a uniform grain refinement within the Stir Zone (SZ), reducing the grain size to approximately 2–3 μm from the initial 15 μm in the base material (BM) irrespective of the probe rotational speeds. After SSFSP, the elongation increased by over 50 % at the cost of 10 % reduction in the ultimate tensile strength for all samples. It was worth to note that variations in tool rotational speed exhibited minimal influence on the microstructure and mechanical properties, offering wide range of probe rotational speeds. This could be attributed to the use of non-rotating shoulder with prob dominated microstructure in the SZ. Fractographic analysis confirmed the ductile nature of fractures, revealing development of fine dimples due to grain refinement. This work underscores the effectiveness of SSFSP in achieving significant grain refinement followed by drastic increase in ductility, which offers valuable insights for using stationary shoulder at wider range of rotational speed.
Subject headings and genre
Added entries (persons, corporate bodies, meetings, titles ...)
-
Patel, Vivek,1983-Högskolan Väst,Avdelningen för svetsteknologi (SV),KAMPT(Swepub:hv)vivpat
(author)
-
Li, WenyaState Key Laboratory of Solidification Processing, Shaanxi Key Laboratory of Friction Welding Technologies, Northwestern Polytechnical University, Xi'an, 710072, Shaanxi (CHN)
(author)
-
Yang, XiaweiState Key Laboratory of Solidification Processing, Shaanxi Key Laboratory of Friction Welding Technologies, Northwestern Polytechnical University, Xi'an, 710072, Shaanxi (CHN)
(author)
-
Andersson, Joel,1981-Högskolan Väst,Avdelningen för svetsteknologi (SV),KAMPT(Swepub:hv)joan0056
(author)
-
Högskolan VästAvdelningen för svetsteknologi (SV)
(creator_code:org_t)
Related titles
-
In:Journal of Materials Research and Technology27, s. 5360-53672238-78542214-0697
Internet link
Find in a library
To the university's database