Electrical properties of GaSb/InAsSb core/shell nanowires

Ganjipour, Bahram (författare)
Lund University,Lunds universitet,Fasta tillståndets fysik,Fysiska institutionen,Institutioner vid LTH,Lunds Tekniska Högskola,Solid State Physics,Department of Physics,Departments at LTH,Faculty of Engineering, LTH
Sepehri, Sobhan (författare)
Dey, Anil (författare)
Lund University,Lunds universitet,Institutionen för elektro- och informationsteknik,Institutioner vid LTH,Lunds Tekniska Högskola,Department of Electrical and Information Technology,Departments at LTH,Faculty of Engineering, LTH
visa fler...
Tizno, Ofogh (författare)
Lund University,Lunds universitet,Fasta tillståndets fysik,Fysiska institutionen,Institutioner vid LTH,Lunds Tekniska Högskola,Solid State Physics,Department of Physics,Departments at LTH,Faculty of Engineering, LTH
Borg, B Mattias (författare)
Dick Thelander, Kimberly (författare)
Lund University,Lunds universitet,Fasta tillståndets fysik,Fysiska institutionen,Institutioner vid LTH,Lunds Tekniska Högskola,Centrum för analys och syntes,Kemiska institutionen,Solid State Physics,Department of Physics,Departments at LTH,Faculty of Engineering, LTH,Centre for Analysis and Synthesis,Department of Chemistry,Faculty of Engineering, LTH
Samuelson, Lars (författare)
Lund University,Lunds universitet,Fasta tillståndets fysik,Fysiska institutionen,Institutioner vid LTH,Lunds Tekniska Högskola,Solid State Physics,Department of Physics,Departments at LTH,Faculty of Engineering, LTH
Wernersson, Lars-Erik (författare)
Lund University,Lunds universitet,Institutionen för elektro- och informationsteknik,Institutioner vid LTH,Lunds Tekniska Högskola,Fasta tillståndets fysik,Fysiska institutionen,Department of Electrical and Information Technology,Departments at LTH,Faculty of Engineering, LTH,Solid State Physics,Department of Physics,Faculty of Engineering, LTH
Thelander, Claes (författare)
Lund University,Lunds universitet,Fasta tillståndets fysik,Fysiska institutionen,Institutioner vid LTH,Lunds Tekniska Högskola,Solid State Physics,Department of Physics,Departments at LTH,Faculty of Engineering, LTH
visa färre...
 (creator_code:org_t)
2014-09-29
2014
Engelska.
Ingår i: Nanotechnology. - : IOP Publishing. - 0957-4484 .- 1361-6528. ; 25:42
Relaterad länk:
http://dx.doi.org/10... (free)
visa fler...
https://lup.lub.lu.s...
https://doi.org/10.1...
visa färre...
  • Tidskriftsartikel (refereegranskat)
Abstract Ämnesord
Stäng  
  • Temperature dependent electronic properties of GaSb/InAsSb core/shell and GaSb nanowires have been studied. Results from two-probe and four-probe measurements are compared to distinguish between extrinsic (contact-related) and intrinsic (nanowire) properties. It is found that a thin (2-3 nm) InAsSb shell allows low barrier charge carrier injection to the GaSb core, and that the presence of the shell also improves intrinsic nanowire mobility and conductance in comparison to bare GaSb nanowires. Maximum intrinsic field effect mobilities of 200 and 42 cm(2) Vs(-1) were extracted for the GaSb/InAsSb core/shell and bare-GaSb NWs at room temperature, respectively. The temperature-dependence of the mobility suggests that ionized impurity scattering is the dominant scattering mechanism in bare GaSb while phonon scattering dominates in core/shell nanowires. Top-gated field effect transistors were fabricated based on radial GaSb/InAsSb heterostructure nanowires with shell thicknesses in the range 5-7 nm. The fabricated devices exhibited ambipolar conduction, where the output current was studied as a function of AC gate voltage and frequency. Frequency doubling was experimentally demonstrated up to 20 kHz. The maximum operating frequency was limited by parasitic capacitance associated with the measurement chip geometry.

Ämnesord

TEKNIK OCH TEKNOLOGIER  -- Nanoteknik -- Nanoteknik (hsv//swe)
ENGINEERING AND TECHNOLOGY  -- Nano-technology -- Nano-technology (hsv//eng)

Publikations- och innehållstyp

art (ämneskategori)
ref (ämneskategori)

Hitta via bibliotek

Till lärosätets databas

Kungliga biblioteket hanterar dina personuppgifter i enlighet med EU:s dataskyddsförordning (2018), GDPR. Läs mer om hur det funkar här.
Så här hanterar KB dina uppgifter vid användning av denna tjänst.

 
pil uppåt Stäng

Kopiera och spara länken för att återkomma till aktuell vy