Structure and thermal expansion of (Cr-x,V1-x)(n+1)AlCn phases measured by X-ray diffraction

Halim, Joseph (författare)
Linköpings universitet,Tunnfilmsfysik,Tekniska fakulteten,Drexel University, PA 19104 USA
Chartier, Patrick (författare)
University of Poitiers, France
Basyuk, Tatyana (författare)
National Academic Science Ukrain, Ukraine
visa fler...
Prikhna, Tatyana (författare)
National Academic Science Ukrain, Ukraine
Caspi, Elad N. (författare)
Nucl Research Centre Negev, Israel
Barsoum, Michel W. (författare)
Drexel University, PA 19104 USA
Cabioch, Thierry (författare)
University of Poitiers, France
visa färre...
 (creator_code:org_t)
ELSEVIER SCI LTD, 2017
2017
Engelska.
Ingår i: Journal of the European Ceramic Society. - : ELSEVIER SCI LTD. - 0955-2219 .- 1873-619X. ; 37:1, s. 15-21
Relaterad länk:
https://urn.kb.se/re...
visa fler...
https://doi.org/10.1...
visa färre...
  • Tidskriftsartikel (refereegranskat)
Abstract Ämnesord
Stäng  
  • MAX phases in the (Crx,V1-x)(n+1)AlCn,system were synthesized by reactive sintering or hot isostatic pressing of elemental powders at temperatures between 1400 degrees C and 1600 degrees C. For n=1, a complete range (0 amp;lt;= x amp;lt;= 1) of solid solutions was found; for n=2 and 3 the solubility ranges were 0.25 amp;lt;= x amp;lt;= 0.75 and 0 amp;lt;= x amp;lt;= 0.5, respectively. Powder X-ray diffraction revealed that the lattice parameters of all (Cr-x,V1-x)(n+1)AlCn solid solutions followed Vegards law. The thermal expansion coefficients of the various compounds were determined from Rietveld refinements of X-Ray patterns obtained at temperatures between ambient and 800 degrees C. For the n=1 and 3 phases the thermal expansion coefficients were almost isotropic; those for the n=2, however, were quite anisotropic with the expansion along the a-axis being significantly larger than along the c-axis. As a general trend, vanadium rich compounds have smaller thermal expansion coefficients than their Cr-rich counterparts. (C) 2016 Elsevier Ltd. All rights reserved.

Ämnesord

TEKNIK OCH TEKNOLOGIER  -- Materialteknik -- Keramteknik (hsv//swe)
ENGINEERING AND TECHNOLOGY  -- Materials Engineering -- Ceramics (hsv//eng)

Nyckelord

MAX phases; Thermal expansion; Carbides; Solid solutions; XRD

Publikations- och innehållstyp

ref (ämneskategori)
art (ämneskategori)

Hitta via bibliotek

Till lärosätets databas

Kungliga biblioteket hanterar dina personuppgifter i enlighet med EU:s dataskyddsförordning (2018), GDPR. Läs mer om hur det funkar här.
Så här hanterar KB dina uppgifter vid användning av denna tjänst.

 
pil uppåt Stäng

Kopiera och spara länken för att återkomma till aktuell vy