The golden alloy Cu5Zn5Al1Sn: Patina evolution in chloride-containing atmospheres

The golden alloy Cu5Zn5Al1Sn : Patina evolution in chloride-containing atmospheres

Chang, Tingru (författare): KTH,Yt- och korrosionsvetenskap,Univ Sci & Technol Beijing, Natl Ctr Mat Serv Safety, Beijing 100083, Peoples R China

Jin, Ying (författare): Univ Sci & Technol Beijing, Natl Ctr Mat Serv Safety, Beijing 100083, Peoples R China.

Odnevall Wallinder, Inger, 1965- (författare): KTH,Yt- och korrosionsvetenskap

(creator_code:org_t)

Elsevier, 2018
2018
Engelska.
Ingår i: Corrosion Science. - : Elsevier. - 0010-938X .- 1879-0496. ; 133, s. 190-203

Relaterad länk:: https://doi.org/10.1...; visa fler...; https://urn.kb.se/re...; https://doi.org/10.1...; visa färre...

Abstract Ämnesord

Stäng

The influence of chloride deposition on the formation, evolution and barrier properties of the patina formed on CuSZn5Al1Sn used for architectural cladding is explored via long-term marine field exposures and laboratory investigations. The presence of Cu2O, ZnO, Al2O3 and SnO2 within the inner part of the patina and intercalation of SnO2, Zn-5(CO3)(2)(OH)(6), Zn6Al2(OH)(16)CO3 center dot 4H(2)O, Zn-5(OH)(8)Cl-2 center dot H2O within its outer part, predominantly composed of Cu-2(OH)(3)Cl, significantly reduce the chloride-induced corrosion compared with Cu metal. The intercalation of zinc-rich corrosion products within the patina and not at the top-surface explain their marginal influence on the runoff process that mainly occurs at the outmost surface.

Av författaren/redakt...: Chang, Tingru; Herting, Gunilla; Jin, Ying; Leygraf, Christo ...; Odnevall Wallind ...

Om ämnet

TEKNIK OCH TEKNOLOGIER: TEKNIK OCH TEKNO ...; och Materialteknik; och Metallurgi och m ...

Kungliga biblioteket hanterar dina personuppgifter i enlighet med EU:s dataskyddsförordning (2018), GDPR. Läs mer om hur det funkar här.
Så här hanterar KB dina uppgifter vid användning av denna tjänst.