Adaptive nanolaminate coating by atomic layer deposition

• Atomic layer deposition (ALD) was used to deposit ZnO/Al2O3/V2O5 nanolaminate coatings to demonstrate a coating system with temperature adaptive frictional behaviour. The nanolaminate coating exhibited excellent conformity and crack-free coating of thickness 110 nm over Inconel 718 substrate. The ALD trilayer coating showed a hardness and elastic modulus of 12 GPa and 193 GPa, respectively. High-temperature tribology of the nanolaminate trilayer was tested against steel ball in dry sliding condition at 25 °C (room temperature, RT), 200 °C, 300 °C, and 400 °C. It was found that the nanolaminate coating showed a low coefficient of friction (COF) and wear rate at RT and 300 °C. The trilayer coating was found intact and stable at all temperatures during the friction tests. The adaptability of nanolaminate coating with the temperature was verified by performing the cyclic friction test at 300 °C and RT. The low COF and wear rate had been attributed to the (100) and (002) basal plane sliding of ZnO top layer, and the interlayer sliding of weakly bonded planes parallel to (001) plane in V2O5 bottom layer. Furthermore, even after the removal of ZnO coating during the tribotest, the bottom V2O5 layer coating stabilized the COF and wear rate at RT and 300 °C.

Ämnesord

NATURVETENSKAP  -- Fysik -- Annan fysik (hsv//swe)

NATURAL SCIENCES  -- Physical Sciences -- Other Physics Topics (hsv//eng)

TEKNIK OCH TEKNOLOGIER  -- Materialteknik -- Annan materialteknik (hsv//swe)

ENGINEERING AND TECHNOLOGY  -- Materials Engineering -- Other Materials Engineering (hsv//eng)

Nyckelord

Atomic layer deposition

Nanolaminate coating

Tribology

High temperature

Adaptive coating

Experimentell fysik

Experimental Physics

Engineering Materials

Materialteknik

Publikations- och innehållstyp

ref (ämneskategori)

art (ämneskategori)