Morphology-Dependent Hardness of Cr7C3-Ni-Rich Alloy Composite vs Orientation Independent Hardness of Cr7C3 Primary Phase in a Laser Clad Microstructure

Venkatesh, Lakshmi Narayanan (författare): Int Adv Res Ctr Powder Met & New Mat ARCI, Hyderabad 500005, Andhra Pradesh, India

Babu, Pitchuka Suresh (författare): Int Adv Res Ctr Powder Met & New Mat ARCI, Hyderabad 500005, Andhra Pradesh, India

Gundakaram, Ravi Chandra (författare): Int Adv Res Ctr Powder Met & New Mat ARCI, Hyderabad 500005, Andhra Pradesh, India

Doherty, Roger D. (författare): Drexel Univ, Dept Mat Engn, Philadelphia, PA 19104 USA

Joshi, Shrikant V., 1960- (författare): Högskolan Väst,Avdelningen för avverkande och additativa tillverkningsprocesser (AAT),PTW

Samajdar, Indradev (författare): Indian Inst Technol, Dept Met Engn & Mat Sci, Mumbai 400076, Maharashtra, India

(creator_code:org_t)

2017-02-10
2017
Engelska.
Ingår i: Metallurgical and Materials Transactions. A. - : Springer Science and Business Media LLC. - 1073-5623 .- 1543-1940. ; 48A:4, s. 1534-1539

Relaterad länk:: https://doi.org/10.1...; visa fler...; https://urn.kb.se/re...; https://doi.org/10.1...; visa färre...

Abstract Ämnesord

Stäng

Microstructural evolution with superheating was studied in chromium carbide-nickel coatings deposited by laser cladding. At lower superheating, selective growth of aOE (c) 0001 > direction from the high density of Cr7C3 grains nucleated resulted in a columnar structure with (0001) texture. Increased superheating lead to the loss of columnar structure as well as the (0001) texture. The hexagonal Cr7C3 showed an unusual isotropic nanoindentation hardness evidently correlated with its low c/a ratio. However, the rod-like morphology of the carbide dendrites resulted in significant anisotropy in the hardness of the composite.

Av författaren/redakt...: Venkatesh, Laksh ...; Babu, Pitchuka S ...; Gundakaram, Ravi ...; Doherty, Roger D ...; Joshi, Shrikant ...; Samajdar, Indrad ...

Om ämnet

TEKNIK OCH TEKNOLOGIER: TEKNIK OCH TEKNO ...; och Materialteknik; och Bearbetnings yt ...

Kungliga biblioteket hanterar dina personuppgifter i enlighet med EU:s dataskyddsförordning (2018), GDPR. Läs mer om hur det funkar här.
Så här hanterar KB dina uppgifter vid användning av denna tjänst.