Good adhesion between chemically oxidized titanium and electrochemically deposited polypyrrole
-
- Idla, K. (författare)
- Laboratory of Physical Chemistry, Tallinn Tech. Univ., Ehitajate T., Tallinn, Estonia
-
- Inganäs, Olle (författare)
- Linköpings universitet,Tekniska högskolan,Biomolekylär och Organisk Elektronik
-
- Strandberg, M. (författare)
- Edison Centre, Pikk 39, 10133, Tallinn, Estonia
-
Laboratory of Physical Chemistry, Tallinn Tech Univ., Ehitajate T., Tallinn, Estonia Tekniska högskolan (creator_code:org_t)
- 2000
- 2000
- Engelska.
-
Ingår i: Electrochimica Acta. - 0013-4686 .- 1873-3859. ; 45:13, s. 2121-2130
- Relaterad länk:
-
https://urn.kb.se/re...
-
visa fler...
-
https://doi.org/10.1...
-
visa färre...
Abstract
Ämnesord
Stäng
- A method for producing extremely adhesive polypyrrole (Ppy) films is described. The electrochemical synthesis of Ppy on thin chemically pre-oxidized Ti layers produces a mechanically strong, shiny polymer film with extremely good adhesion. Adhesion of Ppy films on Ti metal without chemical pre-oxidation is very weak. Two multilayer systems are described with Ppy as an electrochemically active layer, chemically oxidized Ti (TixOy) as a thin adhesive layer, and either a Si-wafer or Al foil as a substrate. Ppy films survive more than 6000 reduction-oxidation cycles in aqueous electrolyte without delamination. The possible mechanisms of enhanced adhesion are discussed. Those are: (1) increased adhesion due to changes in the chemical composition and surface structure of the pre-oxidized Ti, (2) the possibility of the chemical oxidation of pyrrole on the metal surface in addition to the electrochemical polymerization, (3) the adsorption of pyrrole molecules onto pre-oxidized Ti surface by interaction with Ti hydroxides on surface, and (4) the simultaneous growth of TixOy and Ppy.