Sökning: id:"swepub:oai:DiVA.org:liu-50481" > Measurement and mod...
Fältnamn | Indikatorer | Metadata |
---|---|---|
000 | 03922naa a2200553 4500 | |
001 | oai:DiVA.org:liu-50481 | |
003 | SwePub | |
008 | 091011s2005 | |||||||||||000 ||eng| | |
009 | oai:DiVA.org:ltu-2613 | |
009 | oai:DiVA.org:du-17510 | |
024 | 7 | a https://urn.kb.se/resolve?urn=urn:nbn:se:liu:diva-504812 URI |
024 | 7 | a https://doi.org/10.1016/j.msea.2005.02.0262 DOI |
024 | 7 | a https://urn.kb.se/resolve?urn=urn:nbn:se:ltu:diva-26132 URI |
024 | 7 | a https://urn.kb.se/resolve?urn=urn:nbn:se:du-175102 URI |
040 | a (SwePub)liud (SwePub)ltud (SwePub)du | |
041 | a engb eng | |
042 | 9 SwePub | |
072 | 7 | a ref2 swepub-contenttype |
072 | 7 | a art2 swepub-publicationtype |
100 | 1 | a Larsson, Ceciliau Linköpings universitet,Konstruktionsmaterial,Tekniska högskolan,Div. of Eng. Mat., Department of Mech. Eng., Linköping University, 58183 Linköping, Sweden4 aut0 (Swepub:liu)cecla11 |
245 | 1 0 | a Measurement and modeling of residual stress in a welded Haynes® 25 cylinder |
264 | 1 | b Elsevier BV,c 2005 |
338 | a print2 rdacarrier | |
500 | a Validerad; 2005; 20100126 (ysko) | |
520 | a An experimental and simulation study of residual stresses was made in the vicinity of a gas tungsten arc weld, used to join a hemispherical end cap to a cylinder. The capped cylinder is used in a satellite application and was fabricated from a Co-based Haynes® 25 alloy. The cylinder was 34.7 mm in outer diameter and 3.3 mm in thickness. The experimental measurements were made by neutron diffraction and the simulation used the implicit Marc finite element code. The experimental resolution was limited to approximately 3 mm parallel to the axis of the cylinder (the weld was 6 mm in the same direction) and comparison over the same volume of the finite element prediction showed general agreement. Subject to the limited spatial resolution, the largest experimentally measured tensile residual stress was 180 MPa, located at the middle of the weld. However, the predictions suggest that there are regions in the weld where average tensile residual stresses as much as 400 MPa exist. One qualitative disparity between the model and the experiments was that the measurement included a larger degree of asymmetry on either side of the weld than predicted by the model. | |
650 | 7 | a TEKNIK OCH TEKNOLOGIERx Materialteknikx Annan materialteknik0 (SwePub)205992 hsv//swe |
650 | 7 | a ENGINEERING AND TECHNOLOGYx Materials Engineeringx Other Materials Engineering0 (SwePub)205992 hsv//eng |
650 | 7 | a TEKNIK OCH TEKNOLOGIERx Materialteknik0 (SwePub)2052 hsv//swe |
650 | 7 | a ENGINEERING AND TECHNOLOGYx Materials Engineering0 (SwePub)2052 hsv//eng |
653 | a Cobalt | |
653 | a Finite element | |
653 | a Haynes® 25 | |
653 | a Neutron diffraction | |
653 | a Residual stress | |
653 | a Weld | |
653 | a TECHNOLOGY | |
653 | a TEKNIKVETENSKAP | |
653 | a Material Mechanics | |
700 | 1 | a Holden, T.M.u Los Alamos National Laboratory, Los Alamos, NM 87545, USA4 aut |
700 | 1 | a Bourke, M.A.M.u Los Alamos National Laboratory, Los Alamos, NM 87545, USA4 aut |
700 | 1 | a Stout, M.u Los Alamos National Laboratory, Los Alamos, NM 87545, USA4 aut |
700 | 1 | a Teague, J.u Los Alamos National Laboratory, Los Alamos, NM 87545, USA4 aut |
700 | 1 | a Lindgren, Lars-Eriku Högskolan Dalarna,Luleå tekniska universitet,Material- och solidmekanik,Materialteknik4 aut0 (Swepub:du)lel |
710 | 2 | a Linköpings universitetb Konstruktionsmaterial4 org |
773 | 0 | t Materials Science & Engineeringd : Elsevier BVg 399:1-2, s. 49-57q 399:1-2<49-57x 0921-5093x 1873-4936 |
856 | 4 8 | u https://urn.kb.se/resolve?urn=urn:nbn:se:liu:diva-50481 |
856 | 4 8 | u https://doi.org/10.1016/j.msea.2005.02.026 |
856 | 4 8 | u https://urn.kb.se/resolve?urn=urn:nbn:se:ltu:diva-2613 |
856 | 4 8 | u https://urn.kb.se/resolve?urn=urn:nbn:se:du-17510 |