Factors influencing the compressive strength of an injectable calcium sulfate-hydroxyapatite cement.
-
- Nilsson, Malin K (författare)
- Lund University,Lunds universitet,Ortopedi, Lund,Sektion III,Institutionen för kliniska vetenskaper, Lund,Medicinska fakulteten,Orthopaedics (Lund),Section III,Department of Clinical Sciences, Lund,Faculty of Medicine
- Wielanek, L (författare)
-
- Wang, Jian-Sheng (författare)
- Lund University,Lunds universitet,Ortopedi, Lund,Sektion III,Institutionen för kliniska vetenskaper, Lund,Medicinska fakulteten,Orthopaedics (Lund),Section III,Department of Clinical Sciences, Lund,Faculty of Medicine
- visa fler...
- Tanner, K E (författare)
- visa färre...
- (creator_code:org_t)
- 2003
- 2003
- Engelska.
- Ingår i: Journal of Materials Science: Materials in Medicine. - 1573-4838. ; 14:5, s. 399-404
- Tidskriftsartikel (refereegranskat)
Abstract
Ämnesord
Stäng
- A biphasic injectable bone substitute, suitable for filling bone defects, that sets in the body, based on calcium sulfate and hydroxyapatite (HA), is presented. For applications in bone defects the compressive strength is important to assure support of the defect site during loading when the patient is weight bearing. To control the strength, the influence of four different factors; the liquid-to-powder (L/P) ratio, the HA particle morphology, the HA content and the amount of accelerator, were investigated. alpha-Calcium sulfate hemihydrate (CSH) and four different HA powders (three sintered and one spray-dried) were used. All differed in size and morphology. CSH and each HA powder were mixed together with distilled water to form the bone substitute. An accelerator, in form of calcium sulfate dihydrate, was added to the powder phase to obtain an adequate setting time. Cylindrical specimens were compression tested. A lower L/P-ratio gave stronger cement, but was more difficult to inject. The shape and the morphology of the HA particles influenced the strength, and reducing the amount of HA increased the strength. The amount of accelerator (calcium sulfate dihydrate) had no influence. (C) 2003 Kluwer Academic Publishers.
Ämnesord
- TEKNIK OCH TEKNOLOGIER -- Medicinteknik -- Medicinsk material- och protesteknik (hsv//swe)
- ENGINEERING AND TECHNOLOGY -- Medical Engineering -- Medical Materials (hsv//eng)
Publikations- och innehållstyp
- art (ämneskategori)
- ref (ämneskategori)
Hitta via bibliotek
- Journal of Materials Science: Materials in Medicine (Sök värdpublikationen i LIBRIS)
Till lärosätets databas
- 1 av 1
- Föregående post
- Nästa post
- Till träfflistan
Hitta mer i SwePub
- Av författaren/redakt...
- Nilsson, Malin K
- Wielanek, L
- Wang, Jian-Sheng
- Tanner, K E
- Lidgren, Lars
- Om ämnet
-
- TEKNIK OCH TEKNOLOGIER
- TEKNIK OCH TEKNO ...
- och Medicinteknik
- och Medicinsk materi ...
- Artiklar i publikationen
- Journal of Mater ...
- Av lärosätet
- Lunds universitet
Sök utanför SwePub
- Sök vidare i:
- Google Book Search
- Google Scholar
Kungliga biblioteket hanterar dina personuppgifter i enlighet med EU:s dataskyddsförordning (2018), GDPR. Läs mer om hur det funkar här.
Så här hanterar KB dina uppgifter vid användning av denna tjänst.
- Copyright © LIBRIS - Nationella bibliotekssystem
- LIBRIS.kb.se