Zn-doping of GaAs nanowires grown by Aerotaxy

Yang, Fangfang (author)
Lund University,Lunds universitet,Fasta tillståndets fysik,Fysiska institutionen,Institutioner vid LTH,Lunds Tekniska Högskola,Solid State Physics,Department of Physics,Departments at LTH,Faculty of Engineering, LTH
Messing, Maria (author)
Lund University,Lunds universitet,Fasta tillståndets fysik,Fysiska institutionen,Institutioner vid LTH,Lunds Tekniska Högskola,Solid State Physics,Department of Physics,Departments at LTH,Faculty of Engineering, LTH
Mergenthaler, Kilian (author)
Lund University,Lunds universitet,Fasta tillståndets fysik,Fysiska institutionen,Institutioner vid LTH,Lunds Tekniska Högskola,Solid State Physics,Department of Physics,Departments at LTH,Faculty of Engineering, LTH
show more...
Ghasemi, Masoomeh (author)
Lund University,Lunds universitet,Fasta tillståndets fysik,Fysiska institutionen,Institutioner vid LTH,Lunds Tekniska Högskola,Solid State Physics,Department of Physics,Departments at LTH,Faculty of Engineering, LTH
Johansson, Jonas (author)
Lund University,Lunds universitet,Fasta tillståndets fysik,Fysiska institutionen,Institutioner vid LTH,Lunds Tekniska Högskola,Solid State Physics,Department of Physics,Departments at LTH,Faculty of Engineering, LTH
Wallenberg, Reine (author)
Lund University,Lunds universitet,Centrum för analys och syntes,Kemiska institutionen,Institutioner vid LTH,Lunds Tekniska Högskola,Centre for Analysis and Synthesis,Department of Chemistry,Departments at LTH,Faculty of Engineering, LTH
Pistol, Mats-Erik (author)
Lund University,Lunds universitet,Fasta tillståndets fysik,Fysiska institutionen,Institutioner vid LTH,Lunds Tekniska Högskola,Solid State Physics,Department of Physics,Departments at LTH,Faculty of Engineering, LTH
Deppert, Knut (author)
Lund University,Lunds universitet,Fasta tillståndets fysik,Fysiska institutionen,Institutioner vid LTH,Lunds Tekniska Högskola,Solid State Physics,Department of Physics,Departments at LTH,Faculty of Engineering, LTH
Samuelson, Lars (author)
Lund University,Lunds universitet,Fasta tillståndets fysik,Fysiska institutionen,Institutioner vid LTH,Lunds Tekniska Högskola,Solid State Physics,Department of Physics,Departments at LTH,Faculty of Engineering, LTH
Magnusson, Martin (author)
Lund University,Lunds universitet,Fasta tillståndets fysik,Fysiska institutionen,Institutioner vid LTH,Lunds Tekniska Högskola,Solid State Physics,Department of Physics,Departments at LTH,Faculty of Engineering, LTH
show less...
 (creator_code:org_t)
Elsevier BV, 2015
2015
English.
In: Journal of Crystal Growth. - : Elsevier BV. - 0022-0248. ; 414, s. 181-186
Related links:
http://dx.doi.org/10...
show more...
https://lup.lub.lu.s...
https://doi.org/10.1...
show less...
  • Journal article (peer-reviewed)
Abstract Subject headings
Close  
  • Nanowires were grown by means of a novel aerosol-based method called Aerotaxy. Here an aerosol of Au catalyst nanoparticles in N-2 is mixed with MOVPE precursors in a flow-through reactor at atmospheric pressure, whereby nanowires are produced continuously in high concentrations. We demonstrate the possibility of in situ doping of the NWs and the realization of well-controlled p-type GaAs nanowires using this Aerotaxy method. By controlling the cracking and concentration of the precursors, p-doped GaAs nanowires could be grown exhibiting a wide range of Zn doping levels. DEZn was used as the dopant source and the injected DEZn/TMGa ratio was varied from 0.1% to 3.4%. The morphology, the crystalline structure and the composition of the nanowires were studied using SEM, TEM and XEDS. The nanowires were grown straight without any significant tapering and this ideal morphology could be maintained up to an injected DEZn/TMGa ratio of 3.4%. The nanowires typically grew in the [111] direction with a pure zincblende structure, but by increasing the DEZn flow the number of twinning defects increased which we ascribe to Zn incorporation. Elemental analysis shows a high Zn content in the catalyst particle and also a gradient in the Zn content along the nanowire. The samples were analyzed optically using photoluminescence (PL). From the result we estimated the free hole concentration induced by Zn acceptors to be 1 x 10(20) cm(-3) for DEZn/TMGa ratio of 34%. To our knowledge this is the first report on in situ doping of GaAs nanowires grown by Aerotaxy. (C) 2014 Elsevier B.V. All rights reserved.

Subject headings

NATURVETENSKAP  -- Fysik -- Den kondenserade materiens fysik (hsv//swe)
NATURAL SCIENCES  -- Physical Sciences -- Condensed Matter Physics (hsv//eng)
NATURVETENSKAP  -- Kemi (hsv//swe)
NATURAL SCIENCES  -- Chemical Sciences (hsv//eng)
TEKNIK OCH TEKNOLOGIER  -- Nanoteknik -- Nanoteknik (hsv//swe)
ENGINEERING AND TECHNOLOGY  -- Nano-technology -- Nano-technology (hsv//eng)

Keyword

Nanostructures
Metalorganic vapour phase epitaxy
Arsenates
Gallium
compounds
Nanomaterials
Semiconducting III-V materials

Publication and Content Type

art (subject category)
ref (subject category)

Find in a library

To the university's database

  • 1 of 1
  • Previous record
  • Next record
  •    To hitlist

Kungliga biblioteket hanterar dina personuppgifter i enlighet med EU:s dataskyddsförordning (2018), GDPR. Läs mer om hur det funkar här.
Så här hanterar KB dina uppgifter vid användning av denna tjänst.

 
pil uppåt Close

Copy and save the link in order to return to this view