Vanadium Oxide on TiO2(B) - a HREM Study of Catalysis by Support Interaction
-
- Wallenberg, Reine (author)
- Lund University,Lunds universitet,Centrum för analys och syntes,Kemiska institutionen,Institutioner vid LTH,Lunds Tekniska Högskola,Centre for Analysis and Synthesis,Department of Chemistry,Departments at LTH,Faculty of Engineering, LTH
-
- Andersson, Arne (author)
- Lund University,Lunds universitet,Avdelningen för kemiteknik,Institutionen för processteknik och tillämpad biovetenskap,Institutioner vid LTH,Lunds Tekniska Högskola,Division of Chemical Engineering,Department of Process and Life Science Engineering,Departments at LTH,Faculty of Engineering, LTH
-
- Sanati, Mehri (author)
- Lund University,Lunds universitet,Ergonomi och aerosolteknologi,Institutionen för designvetenskaper,Institutioner vid LTH,Lunds Tekniska Högskola,Ergonomics and Aerosol Technology,Department of Design Sciences,Departments at LTH,Faculty of Engineering, LTH
-
(creator_code:org_t)
- 1990
- 1990
- English.
-
In: Ultramicroscopy. - 0304-3991. ; 34:1-2, s. 33-40
- Related links:
-
http://dx.doi.org/10...
-
show more...
-
https://lup.lub.lu.s...
-
https://doi.org/10.1...
-
show less...
Abstract
Subject headings
Close
- A model catalyst system with a loading range between 1/4 to 10 theoretical layers of vanadium oxide on TiO2(B ) support was tried for selective ammoxidation and oxidation of toluene. In the case of ammoxidation, a peak in conversion rate per unit surface area was found for a catalyst with a coverage of about 2 theoretical layers, indicating a strong interaction between the catalyst and the otherwise inactive support. The presence and amount of vanadium oxide on the support surface was verified by diffuse reflectance infrared spectroscopy, energy-dispersive elemental X-ray mapping and chemical analysis. By high resolution electron microscopy, the 32~ volume loss of the K2Ti409 support precursor on calcination was shown to be achieved by formation of microscopic, facetted voids ("negative crystals") in the bulk of the material. Initially, surfaces appeared dean and without any anomalous surface features. This can be explained by similar scattering power of V and Ti, and similar structure types. However, the active phase could be "developed" to visibility by prolonged exposure to the electron beam, which produced 1-2 am particles of reduced vanadium oxides on the surface.
Subject headings
- NATURVETENSKAP -- Kemi (hsv//swe)
- NATURAL SCIENCES -- Chemical Sciences (hsv//eng)
- TEKNIK OCH TEKNOLOGIER -- Kemiteknik (hsv//swe)
- ENGINEERING AND TECHNOLOGY -- Chemical Engineering (hsv//eng)
- TEKNIK OCH TEKNOLOGIER -- Maskinteknik -- Produktionsteknik, arbetsvetenskap och ergonomi (hsv//swe)
- ENGINEERING AND TECHNOLOGY -- Mechanical Engineering -- Production Engineering, Human Work Science and Ergonomics (hsv//eng)
Publication and Content Type
- art (subject category)
- ref (subject category)
Find in a library
To the university's database