Sökning: onr:"swepub:oai:DiVA.org:du-17599" > Corrosion of copper...
Fältnamn | Indikatorer | Metadata |
---|---|---|
000 | 02699naa a2200517 4500 | |
001 | oai:DiVA.org:du-17599 | |
003 | SwePub | |
008 | 150601s2015 | |||||||||||000 ||eng| | |
009 | oai:DiVA.org:kth-166896 | |
024 | 7 | a https://urn.kb.se/resolve?urn=urn:nbn:se:du-175992 URI |
024 | 7 | a https://doi.org/10.1016/j.corsci.2015.03.0092 DOI |
024 | 7 | a https://urn.kb.se/resolve?urn=urn:nbn:se:kth:diva-1668962 URI |
040 | a (SwePub)dud (SwePub)kth | |
041 | a engb eng | |
042 | 9 SwePub | |
072 | 7 | a ref2 swepub-contenttype |
072 | 7 | a art2 swepub-publicationtype |
100 | 1 | a Hultquist, Gunnaru KTH,Yt- och korrosionsvetenskap4 aut0 (Swepub:kth)u1y3z652 |
245 | 1 0 | a Corrosion of copper in distilled water without O-2 and the detection of produced hydrogen |
264 | 1 | b Elsevier BV,c 2015 |
338 | a print2 rdacarrier | |
500 | a QC 20150608 | |
520 | a This paper reports on hydrogen pressures measured during similar to 19,000 h immersion of copper in oxygen-free liquid distilled water. Copper corrosion products have been examined ex-situ by SEM and characterized by XPS and SIMS. XPS strongly indicates a corrosion product containing both oxygen and hydrogen. SIMS shows that oxygen is mainly present in the outer 0.3 mu m surface region and that hydrogen penetrates to depths well below the corrosion product. Thermal desorption spectroscopy shows that the reaction product formed near room-temperature is less stable than that formed in air at 350 degrees C. | |
650 | 7 | a TEKNIK OCH TEKNOLOGIERx Materialteknik0 (SwePub)2052 hsv//swe |
650 | 7 | a ENGINEERING AND TECHNOLOGYx Materials Engineering0 (SwePub)2052 hsv//eng |
650 | 7 | a TEKNIK OCH TEKNOLOGIERx Kemiteknikx Korrosionsteknik0 (SwePub)204022 hsv//swe |
650 | 7 | a ENGINEERING AND TECHNOLOGYx Chemical Engineeringx Corrosion Engineering0 (SwePub)204022 hsv//eng |
653 | a copper | |
653 | a AES | |
653 | a XPS | |
653 | a SIMS | |
653 | a oxidation | |
653 | a hydrogen absorption | |
653 | a Steel Forming and Surface Engineering | |
653 | a Stålformning och ytteknik | |
700 | 1 | a Graham, M. J.4 aut |
700 | 1 | a Kodra, O.4 aut |
700 | 1 | a Moisa, S.4 aut |
700 | 1 | a Liu, R.4 aut |
700 | 1 | a Bexell, Ulfu Högskolan Dalarna,Materialteknik4 aut0 (Swepub:du)ubx |
700 | 1 | a Smialek, J. L.4 aut |
710 | 2 | a KTHb Yt- och korrosionsvetenskap4 org |
773 | 0 | t Corrosion Scienced : Elsevier BVg 95, s. 162-167q 95<162-167x 0010-938Xx 1879-0496 |
856 | 4 8 | u https://urn.kb.se/resolve?urn=urn:nbn:se:du-17599 |
856 | 4 8 | u https://doi.org/10.1016/j.corsci.2015.03.009 |
856 | 4 8 | u https://urn.kb.se/resolve?urn=urn:nbn:se:kth:diva-166896 |
Kungliga biblioteket hanterar dina personuppgifter i enlighet med EU:s dataskyddsförordning (2018), GDPR. Läs mer om hur det funkar här.
Så här hanterar KB dina uppgifter vid användning av denna tjänst.
Kopiera och spara länken för att återkomma till aktuell vy