Environmentally assisted initiation and growth of multiple surface cracks
-
- Hejman, Ulf (författare)
- Malmö högskola,Teknik och samhälle (TS)
-
- Bjerkén, Christina (författare)
- Lund University,Lunds universitet,Malmö högskola,Teknik och samhälle (TS),Materialteknik,Institutionen för maskinvetenskaper,Institutioner vid LTH,Lunds Tekniska Högskola,Materials Engineering,Department of Mechanical Engineering Sciences,Departments at LTH,Faculty of Engineering, LTH
- (creator_code:org_t)
- Elsevier, 2010
- 2010
- Engelska.
- Ingår i: International Journal of Solids and Structures. - : Elsevier. - 0020-7683 .- 1879-2146. ; 47:14-15, s. 1838-1846
- Tidskriftsartikel (refereegranskat)
Abstract
Ämnesord
Stäng
- The initial stages of stress corrosion on an amorphous polymer is investigated. This is done by exposing stressed specimens of polycarbonate to an acetone and water solution. The surface develops two distinct features of degradation that appear on different length scales when subjected to tensile stress. Small pits form on the surface and make it rough. These pits are in the order of micrometers, and are found to be randomly distributed. They occur even without load and seem to slightly increase in number with increasing stress. In the millimeter domain, visible to the bare eye, surface cracks are formed transverse to the direction of loading. The occurrence of cracks is seen to have a positive stress threshold value, exceeding which, a linear increase of number of cracks with stress is found. The manners in which the cracks grow and coalesce on the surface are examined. It is seen that they do not meet crack tip to crack tip. Instead, they avoid each other initially and coalesce crack tip to crack side. The results are discussed in the light of mechanical considerations. A stress analysis for a few configurations of meeting cracks supports the experimental observations. With assumptions of stress corrosion crack growth and coalescence, a simulation of cracks growing from randomly distributed initiation sites is performed. Similar crack patterns as obtained in the experiments are found.
Ämnesord
- TEKNIK OCH TEKNOLOGIER -- Materialteknik -- Metallurgi och metalliska material (hsv//swe)
- ENGINEERING AND TECHNOLOGY -- Materials Engineering -- Metallurgy and Metallic Materials (hsv//eng)
- TEKNIK OCH TEKNOLOGIER -- Materialteknik (hsv//swe)
- ENGINEERING AND TECHNOLOGY -- Materials Engineering (hsv//eng)
Nyckelord
- stress corrosion
- multiple cracking
- experiments
- polycarbonate
- acetone
- crack growth
- Three point bending
- Polycarbonate
- Multiple cracking
- Stress corrosion
- Crack initiation
Publikations- och innehållstyp
- ref (ämneskategori)
- art (ämneskategori)
Hitta via bibliotek
- International Journal of Solids and Structures (Sök värdpublikationen i LIBRIS)
Till lärosätets databas
- 1 av 1
- Föregående post
- Nästa post
- Till träfflistan
Hitta mer i SwePub
- Av författaren/redakt...
- Hejman, Ulf
- Bjerkén, Christi ...
- Om ämnet
-
- TEKNIK OCH TEKNOLOGIER
- TEKNIK OCH TEKNO ...
- och Materialteknik
- och Metallurgi och m ...
-
- TEKNIK OCH TEKNOLOGIER
- TEKNIK OCH TEKNO ...
- och Materialteknik
- Artiklar i publikationen
- International Jo ...
- Av lärosätet
- Malmö universitet
- Lunds universitet
Sök utanför SwePub
- Sök vidare i:
- Google Book Search
- Google Scholar
Kungliga biblioteket hanterar dina personuppgifter i enlighet med EU:s dataskyddsförordning (2018), GDPR. Läs mer om hur det funkar här.
Så här hanterar KB dina uppgifter vid användning av denna tjänst.
- Copyright © LIBRIS - Nationella bibliotekssystem
- LIBRIS.kb.se