Selective deposition of metal oxide nanoflakes on graphene electrodes to obtain high-performance asymmetric micro-supercapacitors

Xia, Zhenyuan, 1983 (författare)
Chalmers tekniska högskola,Chalmers University of Technology
Mishukova, Viktoriia (författare)
Kungliga Tekniska Högskolan (KTH),Royal Institute of Technology (KTH)
Sollami Delekta, Szymon (författare)
Kungliga Tekniska Högskolan (KTH),Royal Institute of Technology (KTH)
visa fler...
Sun, Jinhua, 1987 (författare)
Chalmers tekniska högskola,Chalmers University of Technology
Sanchez Sanchez, Jaime, 1990 (författare)
Chalmers tekniska högskola,Chalmers University of Technology
Li, Jiantong (författare)
Kungliga Tekniska Högskolan (KTH),Royal Institute of Technology (KTH)
Palermo, Vincenzo, 1972 (författare)
Chalmers tekniska högskola,Chalmers University of Technology
visa färre...
 (creator_code:org_t)
2021
2021
Engelska.
Ingår i: Nanoscale. - 2040-3372 .- 2040-3364. ; 13:5, s. 3285-3294
Relaterad länk:
https://research.cha... (primary) (free)
visa fler...
https://doi.org/10.1...
https://research.cha...
https://research.cha...
visa färre...
  • Tidskriftsartikel (refereegranskat)
Abstract Ämnesord
Stäng  
  • To meet the charging market demands of portable microelectronics, there has been a growing interest in high performance and low-cost microscale energy storage devices with excellent flexibility and cycling durability. Herein, interdigitated all-solid-state flexible asymmetric micro-supercapacitors (A-MSCs) were fabricated by a facile pulse current deposition (PCD) approach. Mesoporous Fe2O3 and MnO2 nanoflakes were functionally coated by electrodeposition on inkjet-printed graphene patterns as negative and positive electrodes, respectively. Our PCD approach shows significantly improved adhesion of nanostructured metal oxide with crack-free and homogeneous features, as compared with other reported electrodeposition approaches. The as-fabricated Fe2O3/MnO2 A-MSCs deliver a high volumetric capacitance of 110.6 F cm(-3) at 5 mu A cm(-2) with a broad operation potential range of 1.6 V in neutral LiCl/PVA solid electrolyte. Furthermore, our A-MSC devices show a long cycle life with a high capacitance retention of 95.7% after 10 000 cycles at 100 mu A cm(-2). Considering its low cost and potential scalability to industrial levels, our PCD technique could be an efficient approach for the fabrication of high-performance MSC devices in the future.

Ämnesord

TEKNIK OCH TEKNOLOGIER  -- Naturresursteknik -- Annan naturresursteknik (hsv//swe)
ENGINEERING AND TECHNOLOGY  -- Environmental Engineering -- Other Environmental Engineering (hsv//eng)
NATURVETENSKAP  -- Kemi -- Materialkemi (hsv//swe)
NATURAL SCIENCES  -- Chemical Sciences -- Materials Chemistry (hsv//eng)
TEKNIK OCH TEKNOLOGIER  -- Naturresursteknik -- Energisystem (hsv//swe)
ENGINEERING AND TECHNOLOGY  -- Environmental Engineering -- Energy Systems (hsv//eng)

Publikations- och innehållstyp

art (ämneskategori)
ref (ämneskategori)

Hitta via bibliotek

  • Nanoscale (Sök värdpublikationen i LIBRIS)

Till lärosätets databas

Kungliga biblioteket hanterar dina personuppgifter i enlighet med EU:s dataskyddsförordning (2018), GDPR. Läs mer om hur det funkar här.
Så här hanterar KB dina uppgifter vid användning av denna tjänst.

 
pil uppåt Stäng

Kopiera och spara länken för att återkomma till aktuell vy